Preparation, catalyst

Ziegler catalysts Complex catalysts prepared by interaction between an organometallic derivative and a transition metal derivative. A typical catalyst is the product of the interaction of TiCU and AIBU3. These catalysts polymerize olefins, particularly ethylene, to polyolefins, the polymerization generally being in a siereoregular manner. [Pg.432]

Kiziing M B and Jaras S G 1996 A review of plasma techniques in catalyst preparation and catalytic reactions Appl. Catalysis A 147 1-21... [Pg.2813]

Preparation of palladium - calcium carbonate catalyst. Prepare 60 g. of precipitated calcium carbonate by mixing hot solutions of the appropriate quantities of A.R. calcium chloride and A.R. sodium carbonate. Suspend the calcium carbonate in water and add a solution containing 1 g. of palladium chloride. Warm the suspension until all the palladium is precipitated as the hydroxide upon the calcium carbonate, i.e., until the supernatant liquid is colourless. Wash several times with... [Pg.891]

Phenylpropanolamine. - With catalyst prepared as previously described from 0.5g of palladium chloride and 3g of charcoal, it was possible to reduce two portions of 9.8g of isonitrosopropio-phenone (0.06 mol), dissolved in 150 cc. of absolute alcohol containing 7. Og of hydrogen chloride, to phenylpropanolamine in from 145 - 190 minutes with yields of the isolated chloride from 9.4g to 11. Og, or 84 to 98% of the theoretical. After recrystallization from absolute alcohol the salt melted at 191°. The free base was obtained by treating an aqueous solution of the hydrochloride with alkali on cooling, the liberated amino alcohol solidified and after recrystallization from water melted at 103°."... [Pg.203]

The same regioselective and stereospecific reactions are observed in decalin systems. The 3/3-formate 605 is converted into the a-oriented (j-allylpalladium complex 606, and the hydride transfer generates the fra .s-decalin 607, while the cis junction in 610 is generated from the 3tt-formate 608 by attack of the hydride from the /3-side (609). An active catalyst for the reaction is prepared by mixing Pd(OAc)2 and BU3P in a 1 I ratio with this catalyst the reaction proceeds at room temperature. The reaction proceeded in boiling dioxane when a catalyst prepared from Pd(OAc)2 and BujP in a 1 4 ratio was used[390]. [Pg.373]

Today the most efficient catalysts are complex mixed metal oxides that consist of Bi, Mo, Fe, Ni, and/or Co, K, and either P, B, W, or Sb. Many additional combinations of metals have been patented, along with specific catalyst preparation methods. Most catalysts used commercially today are extmded neat metal oxides as opposed to supported impregnated metal oxides. Propylene conversions are generally better than 93%. Acrolein selectivities of 80 to 90% are typical. [Pg.123]

Patents claiming specific catalysts and processes for thek use in each of the two reactions have been assigned to Japan Catalytic (45,47—49), Sohio (50), Toyo Soda (51), Rohm and Haas (52), Sumitomo (53), BASF (54), Mitsubishi Petrochemical (56,57), Celanese (55), and others. The catalysts used for these reactions remain based on bismuth molybdate for the first stage and molybdenum vanadium oxides for the second stage, but improvements in minor component composition and catalyst preparation have resulted in yields that can reach the 85—90% range and lifetimes of several years under optimum conditions. Since plants operate under more productive conditions than those optimum for yield and life, the economically most attractive yields and productive lifetimes maybe somewhat lower. [Pg.152]

Another group of isoprene polymerization catalysts is based on alanes and TiCl. In place of alkyl aluminum, derivatives of AlH (alanes) are used and react with TiCl to produce an active catalyst for the polymerization of isoprene. These systems are unique because no organometaHic compound is involved in producing the active species from TiCl. The substituted alanes are generally complexed with donor molecules of the Lewis base type, and they are Hquids or soHds that are soluble in aromatic solvents. The performance of catalysts prepared from AlHCl20(C2H )2 with TiCl has been reported (101). [Pg.467]

An additional effect of the use of an organic medium in the catalyst preparation is creation of mote defects in the crystalline lattice when compared to a catalyst made by the aqueous route (123). These defects persist in the active phase and are thought to result in creation of strong Lewis acid sites on the surface of the catalysts (123,127). These sites ate viewed as being responsible for the activation of butane on the catalyst surface by means of abstraction of a hydrogen atom. [Pg.454]

Fig. 2. LP Oxo gas recycle flow scheme A, feedstock pretreatment B, reactor C, catalyst preparation and treatment systems D, condenser E, separator F,...

Oxidation. Carbon monoxide can be oxidized without a catalyst or at a controlled rate with a catalyst (eq. 4) (26). Carbon monoxide oxidation proceeds explosively if the gases are mixed stoichiometticaHy and then ignited. Surface burning will continue at temperatures above 1173 K, but the reaction is slow below 923 K without a catalyst. HopcaUte, a mixture of manganese and copper oxides, catalyzes carbon monoxide oxidation at room temperature it was used in gas masks during World War I to destroy low levels of carbon monoxide. Catalysts prepared from platinum and palladium are particularly effective for carbon monoxide oxidation at 323 K and at space velocities of 50 to 10, 000 h . Such catalysts are used in catalytic converters on automobiles (27) (see Exhaust CONTHOL, automotive). [Pg.51]

Catalyst preparation is more an art than a science. Many reported catalyst preparations omit important details and are difficult to reproduce exacdy, and this has hindered the development of catalysis as a quantitative science. However, the art is developing into a science and there are now many examples of catalysts synthesi2ed in various laboratories that have neady the same physical and catalytic properties. [Pg.174]

The performance of a catalyst often depends as much on the care and method of preparation as on the identity of the active components. This fact has been learned by many who have failed to obtain reproducibiUty among catalyst preparations ia the laboratory or have been responsible for quaUty assurance ia catalyst manufacture. Also, there are many examples of strong effects of trace impurities ia raw material or catalyst support on catalyst performance. [Pg.195]

Polyethylene. Low pressure polymerization of ethylene produced in the Phillips process utilizes a catalyst comprised of 0.5—1.0 wt % chromium (VI) on siUca or siUca-alumina with pore diameter in the range 5—20 nanometers. In a typical catalyst preparation, the support in powder form is impregnated with an aqueous solution of a chromium salt and dried, after which it is heated at 500—600°C in fluid-bed-type operation driven with dry air. The activated catalyst is moisture sensitive and usually is stored under dry nitrogen (85). [Pg.203]

An unusual method for the preparation of syndiotactic polybutadiene was reported by The Goodyear Tire Rubber Co. (43) a preformed cobalt-type catalyst prepared under anhydrous conditions was found to polymerize 1,3-butadiene in an emulsion-type recipe to give syndiotactic polybutadienes of various melting points (120—190°C). These polymers were characterized by infrared spectroscopy and nuclear magnetic resonance (44—46). Both the Ube Industries catalyst mentioned previously and the Goodyear catalyst were further modified to control the molecular weight and melting point of syndio-polybutadiene by the addition of various modifiers such as alcohols, nitriles, aldehydes, ketones, ethers, and cyano compounds. [Pg.531]

Al Ti in the range of 0.9—1.0 appeared optimum for i7j -l,4-polyisoprene yield (20). Other factors such as catalyst preparation temperature, influence of the R group in the alkyl aluminum compound (R Al), and catalyst aging have been extensively studied (16,17). Another variable studied was the effect of... [Pg.4]

Ethylene Oxide Catalysts. Of all the factors that influence the utihty of the direct oxidation process for ethylene oxide, the catalyst used is of the greatest importance. It is for this reason that catalyst preparation and research have been considerable since the reaction was discovered. There are four basic components in commercial ethylene oxide catalysts the active catalyst metal the bulk support catalyst promoters that increase selectivity and/or activity and improve catalyst life and inhibitors or anticatalysts that suppress the formation of carbon dioxide and water without appreciably reducing the rate of formation of ethylene oxide (105). [Pg.458]

The catalyst is previously prepared in an apparatus for catalytic hydrogenation, in which are placed 0.5 g. of palladous chloride, 3.0 g. of Norite, and 20 ml. of distilled water. The bottle is swept out with hydrogen and then shaken with hydrogen for 2-3 hours at 2-3 atmospheres (40 lb.) pressure. The palladium on carbon is collected on a Biichner funnel, washed with five 50-ml. portions of distilled water, then with five 50-ml. portions of 95% ethanol, and finally twice with ether. Upon drying, about 3 g. of the catalyst is obtained. It is stored in a vacuum desiccator over solid sodium hydroxide. If the reduction of the chloro-lepidine does not proceed normally, the used catalyst should be removed by suction filtration and a fresh 3-g. portion of catalyst added. Failure of the reduction step is usually due to an inactive catalyst or to impurities in the acetic acid or chlorolepidine. The palladium catalysts, prepared as described elsewhere in this volume, are presumably also satisfactory for the reduction of 2-chlorolepidine (p. 77). [Pg.46]

Catalysts reduced with formaldehyde carry no adsorbed hydrogen and are less pyrophoric. Barium carbonate as a support may sometimes be advantageous in that the neutrality of the h3 drogenation mixture may be maintained. Barium sulfate or barium carbonate may be a better support than carbon, which may, in some instances, so strongly adsorb the derived product that recovery is difficult or incomplete. Palladium may be more completely and easily recovered from a spent catalyst where carbon rather than barium sulfate is the support. In general, the submitter prefers a catalyst prepared according to procedure C. [Pg.79]

Volume 50 Hydrotreating Catalysts. Preparation, Characterization and Performance. [Pg.263]

The coupling reaction proceeds better when a rigorously degassed Raney nickel catalyst is used, but a nickel catalyst prepared by a much simplifled procedure (Note 9) is also effective. The coupling may also be promoted by other elements, including copper and palladium. [Pg.21]

Catalysis and Surface Science Developments in Chemicals from Methanol, Hydrotreating of Hydrocarbons, Catalyst Preparation, Monomers and Polymers, Photocatalysis and Photovoltaics, edited by Heinz Heinemann and Gabor A. Somorjai... [Pg.673]

Yields obtained from catalyst prepared from 125 gm of aluminum-nickel alloy. In xylene as solvent. [Pg.183]

Rhodium-on-carbon has also been found to bring about the formation of 2,2 -biquinoline from quinoline, the yield and the percentage conversion being similar to that obtained with palladium-on-carbon. On the other hand, rhodium-on-carbon failed to produce 2,2 -bipyridine from pyridine, and it has not yet been tried with other bases. Experiments with carbon-supported catalysts prepared from ruthenium, osmium, iridium, and platinum have shown that none of these metals is capable of bringing about the formation of 2,2 -biquinoline from quinoline under the conditions used with palladium and rhodium. ... [Pg.188]

Kobayashi et al. have reported the use of a chiral lanthanide(III) catalyst for the Diels-Alder reaction [51] (Scheme 1.63, Table 1.26). Catalyst 33 was prepared from bi-naphthol, lanthanide triflate, and ds-l,2,6-trimethylpiperidine (Scheme 1.62). When the chiral catalyst prepared from ytterbium triflate (Yb(OTf)3) and the lithium or sodium salt of binaphthol was used, less than 10% ee was obtained, so the amine exerts a great effect on the enantioselectivity. After extensive screening of amines, ds-1,2,6-... [Pg.40]

A series of chiral boron catalysts prepared from, e.g., N-sulfonyl a-amino acids has also been developed and used in a variety of cycloaddition reactions [18]. Corey et al. have applied the chiral (S)-tryptophan-derived oxazaborolidine-boron catalyst 11 and used it for the conversion of, e.g., benzaldehyde la to the cycloaddition product 3a by reaction with Danishefsky s diene 2a [18h]. This reaction la affords mainly the Mukaiyama aldol product 10, which, after isolation, was converted to 3a by treatment with TFA (Scheme 4.11). It was observed that no cycloaddition product was produced in the initial step, providing evidence for the two-step process. [Pg.160]

A chiral magnesium catalyst prepared from magnesium iodide and 1,2-diphenyl-ethylenediamine was also found to he effective in asymmetric aza Diels-Alder reaction of a-imino ester 21b with 7a (Scheme 5.12) [32]. The novel catalyst was discovered using parallel comhinatorial methods. [Pg.205]

Single crystals of 1 1 complex. °1 1 Catalyst obtained by evaporation of CH2CI2. After 3 months in an open air. Ligand (Ff,Ff)-isopropylidene-2,2 -bis(4-phenyl-oxazoline). Anhydrous complex catalyst prepared from NIBr2 and AgSbFg. [Pg.253]

See also in sourсe #XX -- [ Pg.45 ]

See also in sourсe #XX -- [ Pg.3 , Pg.58 , Pg.69 ]

See also in sourсe #XX -- [ Pg.29 , Pg.175 ]

See also in sourсe #XX -- [ Pg.234 ]

See also in sourсe #XX -- [ Pg.220 , Pg.221 ]

See also in sourсe #XX -- [ Pg.25 , Pg.75 ]

See also in sourсe #XX -- [ Pg.74 , Pg.130 , Pg.148 , Pg.161 ]

See also in sourсe #XX -- [ Pg.35 , Pg.80 , Pg.178 , Pg.179 ]

See also in sourсe #XX -- [ Pg.19 ]

Big Chemical Encyclopedia

Chemical substances, components, reactions, process design ...