1. Introduction

2. Experimental data of PME

2.1. Comparison of the PME in HTSc and metallic superconductors

We start with a comparison of the PME found in bulk Nb disks (see Figure 1a, [26]) with that of HTSc Bi-2212 polycrystalline ceramics (see Figure 1b, [13]) and an artificially patterned YBCO thin film sample (see Figure 1c, [101,102,103]). For all 3 samples, the magnetization is plotted versus temperature, $m\left(T\right)$. The PME is observed when field-cooling (FC-C) or field-warming (FC-W) the sample in a small applied magnetic field. The third cooling mode is zero-field cooling (ZFC), where the sample is cooled in zero field to the lowest temperature, and then a small magnetic field is applied. Also in this mode, signatures of PME may be observed (lower panel of Figure 1b). The features found in Figure 1a–c are, on a first glance, qualitatively the same: In all three cases, there results a positive $m\left(T\right)$ signal, i.e. a paramagnetic signal, when cooling the sample in quite small fields, and the positive $m\left(T\right)$ signal reduces gradually when applying larger magnetic fields. However, it is also quite obvious that the Nb disk exhibits very clear minima ($T_1$)/maxima ($T_p$) on field cooling as well as on warming, whereas these features are less clear in Bi-2212 (Figure 1b) and practically non-existant in the case of the patterned YBCO film (Figure 1c).

In Ref. [104], the authors list some more distinct differences of the PME in Nb and Bi-2212 samples: "Before proceeding to a discussion of our experiment we would like to remark that these two forms of paramagnetism in ceramic Bi-2212 and in a bulk Nb sample can be clearly distinguished in several other ways. For example, the cooling rate affects the magnetic response differently in the two cases. Recent experimental data show significant differences between Nb and granular Bi-2212 HTSc samples. While slow cooling enhances the paramagnetic signal for the granular sample, it is diminished in the Nb sample. This clearly indicates that the equilibrium state of both samples in a small magnetic field is quite different [105]. For the Nb discs Koshelev and Larkin gave an explanation based on the idea that during the cooling process the surface region nucleates superconductivity before the bulk, so that magnetic flux in the sample is compressed and creates an enhanced magnetization [85]. This compressed flux mechanism leads to a metastable state which depends on the cooling procedure whereas the polarization of the spontaneous orbital moments is an equilibrium process. Further, noise measurements of the magnetization of Bi-2212 give signals which are compatible with the presence of spontaneous orbital moments [106]."

The more detailed measurements on the Nb disks performed in the Detroit group in the later years also revealed several important differences between the polycrystalline HTSc samples and the bulk Nb samples like the presence of two characteristic temperatures, $T_1$ and $T_p$ (see the lower panel of Figure 1a), at all applied magnetic fields, and the different shape of the magnetization loops in the temperature range between $T_p$ and $T_c$. This will be discussed in detail in Section 3 below.

Figure 1. Comparison of the experimentally observed PME effect in 3 different types of superconductors. (a). PME in a bulk Nb disk. In the upper graph, the recorded field-cool warming (FC-W) curves are given for small magnetic fields (5 $\mu$T – 966 $\mu$T). The lower graph gives both FC-C and FC-W curves with the applied fields given alongside the respective curves. The arrows indicate the measurement direction. Note here the characteristic minima ($T_1$) and maxima ($T_p$), which are visible up to the highest applied fields. Reprinted with permission from Ref. [26]. (b). PME in a HTSc Bi-2212 polycrystalline, bulk sample. The upper plot shows the field-cool cooling (FC-C) data together with the zero-field cooling (ZFC) curves for several applied magnetic fields. The lower graph of (b) presents the transition region in more detail. Reprinted with permission from Ref. [13,14]. (c). PME observed in an artificially granular HTSc YBCO thin film [101,102,103], see the image of the sample in the upper graph. The lower graph gives the FC-W and ZFC curves obtained on this type of sample. Reprinted with permission from Ref. [101].

Figure 1. Comparison of the experimentally observed PME effect in 3 different types of superconductors. (a). PME in a bulk Nb disk. In the upper graph, the recorded field-cool warming (FC-W) curves are given for small magnetic fields (5 $\mu$T – 966 $\mu$T). The lower graph gives both FC-C and FC-W curves with the applied fields given alongside the respective curves. The arrows indicate the measurement direction. Note here the characteristic minima ($T_1$) and maxima ($T_p$), which are visible up to the highest applied fields. Reprinted with permission from Ref. [26]. (b). PME in a HTSc Bi-2212 polycrystalline, bulk sample. The upper plot shows the field-cool cooling (FC-C) data together with the zero-field cooling (ZFC) curves for several applied magnetic fields. The lower graph of (b) presents the transition region in more detail. Reprinted with permission from Ref. [13,14]. (c). PME observed in an artificially granular HTSc YBCO thin film [101,102,103], see the image of the sample in the upper graph. The lower graph gives the FC-W and ZFC curves obtained on this type of sample. Reprinted with permission from Ref. [101].

The situation of sample (Figure 1c) is completely different: This sample is patterned from an homogeneous YBa${}_2$Cu${}_3$O${}_{7-\delta }$ (YBCO) thin film [101,102], which in its original form did not show any PME. The structure is pictured in the top graph of Figure 1c. The sample does not contain any weak links, which one expects from a granular sample, but the current paths between the individual disks are constricted to a narrow area, where the disks are touching each other. This guarantees the flow of a strong inter-disk current, but with a changed field dependence. Thus, the PME in this sample is only observed at very low applied fields, and entirely caused by trapped flux between the disks. Specific features of the PME like the characteristic temperatures $T_1$ and $T_p$ could not be observed here. Interestingly enough, practically the same situation was encountered recently when investigating the magnetic properties of superconducting YBCO nanofiber mats [107,108], where the supercurrents can flow in local rings as well. Thus, the resulting PME signals resemble the ones of this artificially granular thin film, but with a much smaller signal strength.

In the literature, there is a fourth type of PME reported, the so-called high-field PME or HFPME [109,110,111], which is only observed on HTSc bulk samples of the (RE)BCO-type (where RE= Y, Nd, Eu, Sm, Gd) when measuring superconducting transitions in high applied magnetic fields. The $m\left(T\right)$-signals recorded are first going to negative values at $T_c$, but then start to turn towards positive values at lower temperatures. However, the recorded transitions are fully different from the ones of polycrystalline Bi-2212 [13,14], which suggest a different origin. In Refs. [112,113], we could show that the superconducting transition may be only a small negative contribution to an otherwise positive $m\left(T\right)$-signal when measuring various (RE)BCO bulk superconductors, including GdBCO, NdBCO or a mixture like (Nd,Eu,Gd)BCO (abbreviated: NEG). Especially, GdBCO may show a Néel temperature below 4 K to a ferromagnetic state. So, this high-field PME is caused by such strong paramagnetic magnetic moments inherent to the sample itself.

2.2. Metallic superconducting samples with PME

Figure 2 and Figure 3 present observations of the PME on a variety of metallic superconductors, where FC curves result in positive values of $m\left(T\right)$. In nearly all these measurements, the external magnetic field is applied perpendicular to the sample surface unless noted otherwise (Figure 2a,d and Figure 3a). This also applies to the various measurements on the Nb disks with the exception of Figure 10. However, only some of the authors provide also detailed graphs of the superconducting transition, where some of the characteristic features like in the case of the Nb disks can be seen. Some of the samples investigated are even multilayers where one component may be magnetic, or samples with different amounts of additional doping. Such samples may exhibit positive (paramagnetic) $m\left(T\right)$ signals in the entire temperature range also above the superconducting transition, so the magnetic signals must be worked out properly and be subtracted from the respective plot. This makes the comparison of the curves found in the literature quite difficult. On the other hand, whereever the measurements provide the details close to $T_c$, the characteristic minima and maxima can be observed, which clearly points to the importance of the two characteristic temperatures, $T_1$ and $T_p$.

We further must note here that some of the experiments reported in the literature did only show the presence of PME in their specific system, but some of the experiments done were indeed dedicated and planned experiments to test the theoretical predictions for the occurance of the PME, which nicely reflects that the metallic superconductors are the workhorses for experimentalists.

The PME was observed up to now on a large variety of metallic superconductors including Nb (bulk disks, bars, thin films, as well as nanostructured samples), Pb (on bulk disks, but also in nanowire arrays and Pb-porous glass nanocomposites), mesoscopic structures of Al and Nb [63], Ta, 2H-NbSe${}_2$ single crystals, Nb-AlO${}_x$-Nb tunnel junctions, ZrB${}_{12}$ single crystals, indium-tin oxide films with electrochemical doping (e.g., Mg), Ca${}_3$Rh${}_4$Sn${}_{13}$, Ti-V alloys, Nb-Gd composite thin films, Bi${}_2$Te${}_3$-FeTe heterostructure, Mo${}_{100-x}$Re${}_x$ alloy, Dy${}_{1-x}$Y${}_x$Rh${}_4$B${}_4$, Co/Nb multilayers, Ag/Nb proximity structures, and also the MgB${}_2$ system [70,71,72,73,74,75], which represents the metallic superconductor with the highest transition temperature. Here, we must note that the PME in MgB${}_2$ was always observed in polycrystalline samples (bulks or tapes), where the grain connectivity may be different depending on the chosen preparation route.

Figure 2. PME observed on various metallic superconducting samples I. (a) Rings of In-Sn, measured in FC and ZFC modes (applied field $H=$ 0.2 mT (2 Oe) with the field applied parallel and perpendicular to the sample surface (ZFC (⊥) •, ZFC (‖) , FC (⊥) ∘). The inset shows details of the superconducting transition. Reprinted with permission from Ref. [49]. (b) Pb-films on PEEK, rolled up into cylinders. Data shown are FC curves in various applied fields (0.01 T – 0.3 T). Graph redrawn from the data presented in Ref. [50]. (c) Pb porous. FC and ZFC data are shown for various applied fields. The inset gives the standard measurement at low applied field. Reprinted with permission from Ref. [33]. (d) Ta foil. Shown are the superconducting transitions at $H=$ 30 mT (300 Oe) and for 3 different angles (0${}^{\circ }$, 45${}^{\circ }$ and 90${}^{\circ }$ of the field to the sample surface). Reprinted with permission from Ref. [35]. (e) ZrB${}_{12}$ crystals, measured at 0.1 mT (1 Oe), 0.5 mT (5 Oe), and 1.5 mT (15 Oe) applied field. The insets give details of the transition at 5 $\mu$T (0.05 Oe) (FFC-W), 0.5 mT (5 Oe) (FFC-W and ZFC) and 5 mT (50 Oe) (SFC-C), where the F stands for ‘fast’ and S for ‘slow’. Reprinted with permission from Ref. [37]. (f) Susceptibility of an Al mesoscopic disk (2.5 $\mu$m dia., thickness 0.1 $\mu$m) at applied fields of 0.9, 3.5, 4.0, 6.5 and 12 mT (9, 35, 40, 65 and 120 G). The last 4 curves were multiplied by a factor of 10. The authors point out that there is no hysteresis when cooling/warming. Reprinted with permission from Ref. [63].

Figure 2. PME observed on various metallic superconducting samples I. (a) Rings of In-Sn, measured in FC and ZFC modes (applied field $H=$ 0.2 mT (2 Oe) with the field applied parallel and perpendicular to the sample surface (ZFC (⊥) •, ZFC (‖) , FC (⊥) ∘). The inset shows details of the superconducting transition. Reprinted with permission from Ref. [49]. (b) Pb-films on PEEK, rolled up into cylinders. Data shown are FC curves in various applied fields (0.01 T – 0.3 T). Graph redrawn from the data presented in Ref. [50]. (c) Pb porous. FC and ZFC data are shown for various applied fields. The inset gives the standard measurement at low applied field. Reprinted with permission from Ref. [33]. (d) Ta foil. Shown are the superconducting transitions at $H=$ 30 mT (300 Oe) and for 3 different angles (0${}^{\circ }$, 45${}^{\circ }$ and 90${}^{\circ }$ of the field to the sample surface). Reprinted with permission from Ref. [35]. (e) ZrB${}_{12}$ crystals, measured at 0.1 mT (1 Oe), 0.5 mT (5 Oe), and 1.5 mT (15 Oe) applied field. The insets give details of the transition at 5 $\mu$T (0.05 Oe) (FFC-W), 0.5 mT (5 Oe) (FFC-W and ZFC) and 5 mT (50 Oe) (SFC-C), where the F stands for ‘fast’ and S for ‘slow’. Reprinted with permission from Ref. [37]. (f) Susceptibility of an Al mesoscopic disk (2.5 $\mu$m dia., thickness 0.1 $\mu$m) at applied fields of 0.9, 3.5, 4.0, 6.5 and 12 mT (9, 35, 40, 65 and 120 G). The last 4 curves were multiplied by a factor of 10. The authors point out that there is no hysteresis when cooling/warming. Reprinted with permission from Ref. [63].

Figure 3. PME observed on various metallic superconducting samples II. (a) Pb nanowire arrays. ZFC curves of a sample with $d=$ 40 nm for 5, 8 and 11 mT (50, 80 and 110 Oe). H is applied along the long axis of the wire. Reprinted with permission from Ref. [53]. (b) 2H-NbSe${}_2$ single crystals. H (‖a,b)= 5 mT (50 Oe). The $M\left(T\right)$ plots in the vicinity of $T_c$. Paramagnetic signals are evident in all three modes (ZFC, FC-C, FC-W), and $T_p<T_c$. Reprinted with permission from Ref. [41]. (c) Bi/Ni-bilayers. The FC results are measured in magnetic fields in the range ±5 mT (50 Oe).The signals from the Ni layer and the substrate are subtracted in all data shown. Reprinted with permission from Ref. [60]. (d) MgB${}_2$ polycrystalline bulk sample. FC magnetization curves at different applied fields. The PME is observable up to 25 $\mu$T (250 mOe). Reprinted with permission from Ref. [71]. (e) Superconductor/ferromagnet heterostructure V(40 nm)/Fe(1.1 nm). Temperature dependence of the magnetic moment around $T_c$ measured in different magnetic fields and cooling regimes (FC, ZFC). The inset shows the field dependence of the induced magnetic moment in the FC regime. Reprinted with permission from Ref. [57]. (f) Sn${}_{90}$In${}_{10}$ alloy in form of a cylinder with 3 different phases ($\beta$-InSn, $\gamma$-InSn, $\beta$-Sn). The graph gives the FC curves for two samples annealed at 340 K and 380 K. Reprinted with permission from Ref. [34].

Figure 3. PME observed on various metallic superconducting samples II. (a) Pb nanowire arrays. ZFC curves of a sample with $d=$ 40 nm for 5, 8 and 11 mT (50, 80 and 110 Oe). H is applied along the long axis of the wire. Reprinted with permission from Ref. [53]. (b) 2H-NbSe${}_2$ single crystals. H (‖a,b)= 5 mT (50 Oe). The $M\left(T\right)$ plots in the vicinity of $T_c$. Paramagnetic signals are evident in all three modes (ZFC, FC-C, FC-W), and $T_p<T_c$. Reprinted with permission from Ref. [41]. (c) Bi/Ni-bilayers. The FC results are measured in magnetic fields in the range ±5 mT (50 Oe).The signals from the Ni layer and the substrate are subtracted in all data shown. Reprinted with permission from Ref. [60]. (d) MgB${}_2$ polycrystalline bulk sample. FC magnetization curves at different applied fields. The PME is observable up to 25 $\mu$T (250 mOe). Reprinted with permission from Ref. [71]. (e) Superconductor/ferromagnet heterostructure V(40 nm)/Fe(1.1 nm). Temperature dependence of the magnetic moment around $T_c$ measured in different magnetic fields and cooling regimes (FC, ZFC). The inset shows the field dependence of the induced magnetic moment in the FC regime. Reprinted with permission from Ref. [57]. (f) Sn${}_{90}$In${}_{10}$ alloy in form of a cylinder with 3 different phases ($\beta$-InSn, $\gamma$-InSn, $\beta$-Sn). The graph gives the FC curves for two samples annealed at 340 K and 380 K. Reprinted with permission from Ref. [34].

Figure 2a–f and Figure 3a–f give several experimental results on various metallic superconductors. Table 1 lists all PME experiments on metallic superconductors, together with the data for the superconducting transition temperature (onset), the recorded transition width $\Delta T_c$, $\kappa$, the references and some remarks to the experiment itself. Especially the PME observations on mesoscopic metallic superconductors (Al, Nb) [63,65] gave very important input to the understanding of the PME. The same applies to the measurements on ZrB${}_{12}$ crystals with an unique vortex-vortex interaction [37], making the material an intermediate 1.5-type superconductor. This we will discuss in Section 5 in detail.

And, of course, samples of the metallic superconductors are much better suited than HTSc materials (deposition of clean thin films, patterning) to attempt the various types of magnetic imaging of the vortex structures as we will see later in Section 4 below.

After the first observations of the PME in the Bi-2212 HTSc, the work in this direction also continued. Here, we list only some of the contributions as this could be the topic of an own, dedicated review. Even more details on the superconducting transitions of Bi-2212 were worked out [118,119], and several more types of HTScs were found to exhibit the PME like YBCO as thin films, polycrystalline bulks, single crystals or nanofiber mats [17,107,108,120,121,122,123], La${}_{1-x}$Sr${}_x$CuO${}_4$[124], the electron-doped superconductor Nd${}_{2-x}$Ce${}_x$CuO${}_y$[125], the bismuthate Ba${}_{1-x}$K${}_x$BiO${}_3$[126] and RSr${}_2$Cu${}_2$NbO${}_{7-\delta }$ compounds (R= Y, Pr, and Gd), which have a crystallographic structure like YBCO [127]. Furthermore, the PME was observed in measurements of the iron-based superconductors (IBS) like K${}_{0.8}$Fe${}_{1.7}$Se${}_2$[128]. An important issue we must note here is that all these HTSc materials mentioned here are typically granular, and most of the samples studied are such with $T_c<$ 77 K.

Table 1. Metallic superconductors exhibiting the PME. Given are the varoius materials, the sample type, the superconducting transition temperature, $T_c$, in Kelvin, the transition width, $\Delta T_c$, the Ginzburg-Landau parameter $\kappa$, the respective citations and some remarks to the experiment. The abbreviation nps denotes nanoparticles, ⌀ stands for diameter and ITO = Indium Tin Oxide.

Table 1. Metallic superconductors exhibiting the PME. Given are the varoius materials, the sample type, the superconducting transition temperature, $T_c$, in Kelvin, the transition width, $\Delta T_c$, the Ginzburg-Landau parameter $\kappa$, the respective citations and some remarks to the experiment. The abbreviation nps denotes nanoparticles, ⌀ stands for diameter and ITO = Indium Tin Oxide.

name	type	${\mathit{T}}_{\mathit{c}}$	$\mathit{\Delta }{\mathit{T}}_{\mathit{c}}$	$\mathit{\kappa }$	citation	remarks
Nb bulk	commercial	9.26	∼0.1	–	[25,30,31,32,114,115,116,117]	stationary sample, SQUID
Nb bulk	from ingot	9.25	0.05–0.1	∼1	[27]	several types of samples,
						disk-shaped, 3–6 mm ⌀
Nb	calculated	–	–	–	[39,40]	disks, cylinders
Nb	crystal, poly	9.38	–	–	[35]	Nb crystal bar, polycryst. disks
Ag-Nb	wires	9.2	–	–	[64]	Nb-wires with Al sheath
Nb	films	9.2	0.03	–	[91]	strain-free thin films
Nb	films	8.8/8.3	–	–	[52]	thin films, relaxation
Nb-Gd	films	8.85/4	–	–	[54]	Gd-doped Nb films, various doping
nano-Nb	Nb powder+corund	–	–	–	[44]	granular Nb with various pore sizes
Nb/Cu	multilayers	9.25	0.3	–	[51]	PME, AC frequency dep.
Nb/Co	multilayers	9.2	–	–	[55]	Co-layer top/bottom of Nb (240 nm)
Au-Ho-Nb	trilayer	8.52	0.3	–	[56]	$\mu$SR-study
Nb-AlOx-Nb	multiply connected	–	–	–	[58,59]	Josephson junction arrays
Pb	films on PEEK	7.2	0.1	–	[50]	rolled up as cylinders
Pb-glass	porous glass	7.2	∼0.5	–	[33]	85 % filling of pores with Pb
Pb-nw	NWs 40nm dia	7.2/4	–	–	[53]	filled alumina template
Pb-Co	nanocomposite	6.2	–	–	[62]	Pb thin film with 1 vol-% Co
Al	thin film/disks	1.1	0.7	0.3	[63]	Al and Nb mesoscopic structures
Al	disk 1.5 $\mu$m ⌀	–	–	–	[65]	Al mesoscopic disk, 0.03 K
Ta	foil	4.38	–	1.39	[35]	Ta foil
Bi/Ni	Ni layer on top	3.9	0.1	–	[60]	PME in positive/negative fields
NbSe${}_2$	single crystals	7.15	broad	–	[41]	very clean crystals
Ca${}_3$Rh${}_4$Sn${}_{13}$	single crystals	8.4	∼ 2.5	–	[46]	SQUID-VSM with various amplitudes
Dy${}_{(1-x)}$Y${}_x$Rh${}_4$B${}_4$	crystals	∼ 6	0.5	–	[36]	various contents x tested
LiRhB	polycrystalline	2,4-2,6	–	1	[47]	different composition, partly 2 $T_c$’s
Bi${}_2$Te${}_3$-FeTe	bilayer	∼ 6	–	–	[61]	Bi${}_2$Te${}_3$ (9 nm)/FeTe (140 nm)
In-Sn	cylinders, 3 phases	6.2/4.7/3.7	0.2	–	[34]	$\beta$-InSn, $\gamma$-InSn, $\beta$-Sn → extrinsic PME
In-Sn-O	films, Mg-dop.	4.81	0.09	–	[49]	doped ITO with Mg, 90/10
Mo${}_{100-x}$Re${}_x$	bulk	4.47	–	–	[45]	high-field PME
Ti${}_{0.8}$V${}_{0.2}$	bulk	4.15	0.2	–	[38]	high-field PME
V/Fe	bilayers	3.3–3.5	–	11–20	[57]	40.1 nm V / 1.1 nm Fe
ZrB${}_{12}$	crystals	5.95	0.08	0.8	[37]	type II-1 sc., vortex interaction
B-doped diamond	thin film	5.8–2.1	–	–	[76]	various doping
MgB${}_2$	granular	38.2	∼ 2	–	[70]	bulk/powder
MgB${}_2$	granular/sintered	38	∼ 2	–	[71]	bulk, $\gamma$-irradiation
MgB${}_2$	TiO${}_2$ np	–	–	29.1	[72,73]	2 % TiO${}_2$
MgB${}_2$	tapes	35–29.9	∼5	–	[74]	Fe-sheated tapes with Co${}_3$O${}_4$ nps
MgB${}_2$	MgO	37.1/38.8	15/0.5	–	[75]	MgO ∼ 40%/ ∼ 7.3 %

Thus, the metallic superconductors represent a large playground for the observation of the PME in clearly non d-wave superconductors. This also applies for the measurements in MgB${}_2$, representing a two-band superconductor with all tunable inter-grain properties [69,129,130]. Interestingly enough, there are no observations of the PME reported in granular systems like metallic superconductor wires of NbTi or Nb${}_3$Sn, which may be a consequence of the strong coupling between the grains in these materials [7,131].

2.3. Apparatus

Before starting the discussion of the PME observations, it is instructive to have a look at the measurement apparatus employed by the various groups. Various experimental techniques were applied to observe the PME in superconductors. As the Meissner effect describes the magnetic phase transition of a material to the superconducting state at a given applied field (see also the phase diagram in Figure 9 below), the use of magnetometry is the most natural approach, and, as the signals to be expected may be very small close to $T_c$, a superconducting quantum interference device (SQUID) magnetometer is the most appropriate choice. However, several other measurement methods were employed in the literature like the vibrating sample magnetometer (VSM), extraction magnetometer, Faraday balance and AC susceptometer, all both commercial and custom-built. Magnetic imaging techniques – magneto-optic imaging (Faraday effect), scanning Hall probe(s) and scanning SQUID techniques – were used to study the PME near the superconducting transition regime.

Here, it is important to give some comments to the most widely used method; SQUID magnetometry. In early stages of the PME experiments, there were discussions whether the observed PME is actually from the sample or just an artifact of the measurement technique. Blunt et al. [12] demonstrated that spurious trapped fields in a superconducting magnet system can lead to a paramagnetic superconducting transition, which is in fact, just a mirror image (mirrored at the temperature axis) of the normal diamagnetic situation. Thus, this situation can be exclude to be a manifestation of PME. Another such report was presented by Atzmony et al. [132], which clearly indicated that the paramagnetic signals observed on a bulk YBCO sample with strong flux pinning were just an artifact arising from the presence of a small field gradient. When measuring the same sample in an extraction magnetometer, these paramagnetic signals were gone.

Figure 4. Comparison of $m\left(H\right)$ data achieved using the stationary sample technique versus the moving sample in standard SQUID. The data were measured at Detroit at a temperature $T=$ 9.08 K. () Conventional QD SQUID measurement with moving sample and field generated by the superconducting magnet. () The magnetic moment is evaluated directly from the SQUID voltage, whereas the field was generated by a copper coil. More details on such magnetization loops will be discussed in Section 3.3 below. (a) Comparison of hysteresis loops measured by the two methods, sample Nb1. (b) Comparison of the virgin curves and their merging to the main hysteresis loops, sample Nb1.

Figure 4. Comparison of $m\left(H\right)$ data achieved using the stationary sample technique versus the moving sample in standard SQUID. The data were measured at Detroit at a temperature $T=$ 9.08 K. () Conventional QD SQUID measurement with moving sample and field generated by the superconducting magnet. () The magnetic moment is evaluated directly from the SQUID voltage, whereas the field was generated by a copper coil. More details on such magnetization loops will be discussed in Section 3.3 below. (a) Comparison of hysteresis loops measured by the two methods, sample Nb1. (b) Comparison of the virgin curves and their merging to the main hysteresis loops, sample Nb1.

A very useful documentation for experimentalists was presented by McElfresh [133], discussing the various problems which may appear when using SQUID magnetometers to measure the superconducting transition.

Due to these obvious problems with magnetometry of small magnetic signals, all major results obtained by the groups in Cologne (on polycrystalline Bi-2212 samples) and Detroit (bulk Nb disk samples) were measured using a commercial SQUID magnetometer [134] using the technique of a stationary sample [26,31,135]. The sample in the form of disk was positioned at the center of the second-order gradiometric detector coil in the SQUID magnetometer. The sample plane was perpendicular to the magnetic field generated by a which is a part of the ultra-low-field option of the commercial magnetometer (Quantum Design, [134]). To avoid any residual flux trapped in the surrounding superconducting magnet, the entire magnet system was warmed above its superconducting transition temperature and the superconducting magnet was never energized until the completion of all low-field measurements. During both temperature and field measurements, the sample was kept stationary, thereby eliminating any spurious signals that might have arisen from field inhomogeneities with sample position. The maximum field generated by the Cu solenoid was only 1 mT to prevent possible damage of the coil. The available field range was also limited by the range within which the SQUID voltage can be measured. The major contribution to the SQUID voltage was from magnetic flux change due to magnetic field change and the signal from the sample was relatively much smaller. The field range $\pm 1$ mT used in this work is both safe for the Cu coil ($I_{\max }=$ 0.2 A) and also the field-induced SQUID voltage was always within the range covered by the SQUID electronics.

These measurements were controlled by low-level programs written in the EDC language [134] The analog voltage output from the SQUID amplifier is proportional to the magnetic flux change through the pickup coils. During the temperature-dependent measurements at constant field the magnetic flux change through the pickup coils is only due to the relative changes of magnetic moment of the measured sample and the SQUID voltage can be directly transformed into magnetic moment values.

The 5 T superconducting magnet build in the magnetometer system was not used to generate field to avoid problems caused to flux trapping in this magnet, in particular inhomogeneity of trapped field and flux relaxation, i.e., time-dependent decay of magnetic field. To avoid even residual flux trapped in this magnet from previous measurements, all the low-field measurements discussed in this paper were done only after preceding warming up of all the system with superconducting magnet. The only way how this magnet (permanently switched off during all the measurements since the last warm-up of the system) affected magnetic field at the sample position was by partial screening the stray field generated around the small Cu coil.

Here, we present a discussion of some more details of the measurement system operated in Detroit, which was essential for the discovery of the PME in Nb. The magnetic field H at sample position was during the standard system operation (i.e., when the 5 T superconducting magnet immersed in liquid Helium was not used but it was in the superconducting state) proportional to the current as

$$H=C_{\mathrm{H}}I$$

(1)

In the system in Detroit $C_{\mathrm{H}}=$ 4.83 mT/A so that the maximum field was $H_{\max }=C_{\mathrm{H}}{I}_{\max }=$ 0.966 mT for $I_{\max }=$ 200 mA. The effect of screening by the superconducting magnet is significant: the field generated by the copper coil was nearly two times larger when the 5 T superconducting magnet was in the normal state and easily penetrated by stray field from the copper coil. In such a case, $C_{\mathrm{H}}=$ 8.2 mT/A. Even without any sample in the pick-up SQUID coil, the SQUID voltage changes due to an improper balance of the gradiometric coils when the external magnetic field is changed. This field-dependent background voltage has to be subtracted from a measured signal to obtain the true signal due to the relative changes of the magnetic moment of a sample placed inside the SQUID pick-up coil. The background voltage can be also expressed formally as a virtual magnetic moment with the susceptibility ${\chi }_b$. For this system, ${\chi }_b$ = 0.003622 emu/Oe = 0.03622 Am${}^2$/T, so for the maximum field $H_{\max }=$ 0.966 mT the moment to be formally subtracted is as large as ${\chi }_b{H}_{\max }=$ 0.035 emu.

Before a measurement of a magnetic hysteresis loop (MHL), the sample was cooled from normal to superconducting state in zero field and so that one can well assume that the magnetic moment of the sample stays zero as long as zero field is kept. When a magnetic field is applied, the SQUID voltage changes due to both the background field-induced voltage and the magnetic moment induced in the sample. The actual moment, m, of the measured sample is evaluated from the SQUID voltage, U, using the expression

$$m=C_m(U-q_{b}H-U_0),$$

(2)

where $U_0$ denotes the SQUID voltage after cooling the sample in zero field that corresponds to zero magnetic moment.

It should be noted that this is a way of evaluation of only relative changes of the magnetic moment with respect to a reference starting value. The resolution of such moment evaluation is limited mainly by noise in the relatively large background SQUID voltage. The sensitivity of moment measurement using the above described method is better than 10${}^{-6}$ emu.

Complementary measurements in magnetic fields larger than 1 mT were done as "standard" magnetization measurements using the built-in 5 T superconducting magnet to generate the applied field. Though the superconducting magnet was used to generate the field, it was never charged up to higher fields before and during the measurements to minimize the amount of flux pinned in the magnet itself. The sample was moving during (only) these measurements, but the scan length was set below 1 cm. In the overlapping range of fields and moment values, the results from both methods were close to each other which illustrates the validity of the low field procedure. The comparison of the moving () and stationary sample () during an MHL run is depicted in Figure 4. The results of this comparison enabled then the further measurements of the PME on more standard magnetometers as the specific features of the PME curves were known. Of course, the reduced scan length was kept for all further measurements of the PME on different SQUID systems (Tokyo, Nancy).

Knowing the situation of the PME measured by a stationary sample, one could also employ the standard measurement mode of the SQUID magnetometer, e.g., to reach much higher applied magnetic fields. One way out of the problem was for many researchers to operate the PME measurements just after the coil system of the magnetometer was warmed up to room temperature to avoid any kind of trapped flux in the coil system. Another very useful feature was the constant temperature sweep mode, available first with the QD XL-SQUID line, allowing to record the superconducting transitions with controlled temperature sweep rate. Measurements of this type were done by us in Tokyo using a 7T-XL SQUID system [112].

3. Specific measurements, details of the superconducting transitions of Nb disks and discussion

Figure 5. Details of $m\left(T\right)$ transitions measured on a punched Nb disk. Measurements performed at Detroit. (a). Superconducting transitions measured in small applied magnetic fields (10, 50, 100, 200 $\mu$T) generated by the Cu coil (low-field option). The arrows indicate the direction of te measurement (FC-C and FC-W). The temperature $T_p$ is defined here as the temperature of the maximum m. The inset shows the definition of the temperature $T_1$ as the lowest m recorded on the diamagnetic side. Figure reprinted with permission from Ref. [114]. (b). FC-C and FC-W curves recorded to various lowest temperatures as indicated in the graph, ranging between 8.2 K and 8.9 K. The characteristic temperatures $T_p$ and $T_1$ are indicated by red and blue arrows, respectively. The inset gives the details around $T_1$.

Figure 5. Details of $m\left(T\right)$ transitions measured on a punched Nb disk. Measurements performed at Detroit. (a). Superconducting transitions measured in small applied magnetic fields (10, 50, 100, 200 $\mu$T) generated by the Cu coil (low-field option). The arrows indicate the direction of te measurement (FC-C and FC-W). The temperature $T_p$ is defined here as the temperature of the maximum m. The inset shows the definition of the temperature $T_1$ as the lowest m recorded on the diamagnetic side. Figure reprinted with permission from Ref. [114]. (b). FC-C and FC-W curves recorded to various lowest temperatures as indicated in the graph, ranging between 8.2 K and 8.9 K. The characteristic temperatures $T_p$ and $T_1$ are indicated by red and blue arrows, respectively. The inset gives the details around $T_1$.

3.1. Investigated Nb samples

The samples originally measured in Detroit were Nb disks of 6.4 mm in diameter, which were punched from commercially available, 0.127-mm thick sheets (99.98 % purity, Johnson-Matthey) [25,26]. In addition, the optical and electron microscopy investigations on these Nb disks punched from cold-rolled 0.127-mm thick Nb sheets also indicate the presence of surface defects and voids.

Table 2. Summary of the Nb disks samples measured in Detroit. Given are the sample names, their origin, some comments, the sample dimensions and the measured data for $T_{c,\mathrm{onset}}$, $T_p$ and $T_1$.

Table 2. Summary of the Nb disks samples measured in Detroit. Given are the sample names, their origin, some comments, the sample dimensions and the measured data for $T_{c,\mathrm{onset}}$, $T_p$ and $T_1$.

sample	Nb1	Nb2	Nb3	Nb4
sample origin	D4S2	D2S2	D10S2-1	DI08-1
Comment	“basic”	abraded	edge sand	implanted
PME	yes	no	yes	yes
radiusr (mm)	3.2	3.2	3.2	3.2
thicknesst ($\mu$m)	127	∼110	127	250
$T_{c,\mathrm{onset}}$ (K)	9.20	9.26	9.24	9.28
$T_1$ (K)	9.15	n/a	9.24	9.17(5)
$T_p$ (K)	9.05(5)	n/a	9.06(5)	9.08

The results presented in the following Figure 5, Figure 6 and Figure 7 are for one particular Nb disk (sample Nb1, stemming from Nb sheet D4S2), see also Ref. [25]. One of the original Nb sheets (D4S2) and some punched disks (samples named Nb001–Nb005) were carried to Tokyo (SRL/ISTEC, Div. 3) for further measurements in different magnetometers, and finally to IJL Nancy, France, where the same material was studied again nearly 25 years later using SQUID magnetometry and AC susceptibility measurements.

Figure 6. PME on a bulk Nb disk (from sheet D4S2, 127 $\mu$m thick, 3.2 mm radius). (a). FC-C and FC-W curves on the Nb disk in various applied magnetic fields ranging between 1 and 15 mT. (b). Figure shows the FC-C and FC-W curves only at 1, 2, 6 and 12 mT for clarity. (c). High-field (20, 40, 60, 120 and 140 mT) FC-C and FC-W curves on the same Nb sample. Note that a paramagnetic peak is reached in the FC-C curves at $T_{pc}$, and the FC-W curves show a peak ($T_{pw}$) and minimum ($T_{1w}$) in all applied magnetic fields. $T_{pc}$ and $T_{pw}$ correspond very well, whereas $T_{1c}$ and $T_{1w}$ show a distinct difference (see also Figure 9 below).

Figure 6. PME on a bulk Nb disk (from sheet D4S2, 127 $\mu$m thick, 3.2 mm radius). (a). FC-C and FC-W curves on the Nb disk in various applied magnetic fields ranging between 1 and 15 mT. (b). Figure shows the FC-C and FC-W curves only at 1, 2, 6 and 12 mT for clarity. (c). High-field (20, 40, 60, 120 and 140 mT) FC-C and FC-W curves on the same Nb sample. Note that a paramagnetic peak is reached in the FC-C curves at $T_{pc}$, and the FC-W curves show a peak ($T_{pw}$) and minimum ($T_{1w}$) in all applied magnetic fields. $T_{pc}$ and $T_{pw}$ correspond very well, whereas $T_{1c}$ and $T_{1w}$ show a distinct difference (see also Figure 9 below).

3.2. Observation of PME – superconducting transitions

In this Section, we focus on the detailed measurements performed on various Nb disk samples, which were found to exhibit the most clear PME behavior. Niobium (Nb) has an bcc lattice ($a=$ 0.33 nm and $\alpha =\beta =\gamma$), is isotropic, and represents a classical s-wave superconductor with a Ginzburg-Landau parameter $\kappa$ close to the border between type-I and type-II superconductors ($\kappa \sim$0.8–1.0).

The Nb sample studied in Detroit (similarly to some other bulk Nb samples seen in the literature) shows a very specific behavior around the superconducting transition region. In previous papers [25,27], this behavior was in detail studied mainly using the field-cooled cooling (FC-C) and field-cooled warming (FC-W) curves, i.e., the temperature dependence of magnetic moment $m\left(T\right)$ was measured at constant magnetic field when temperature is slowly continuously swept from a temperature where the sample is in normal state down to a temperature well below the superconducting transition (FC-C) and then the temperature sweep direction is reversed (FC-W). These scans of the magnetic moment, $m\left(T\right)$, reveal several characteristic temperatures, namely $T_1(<T_{c,\mathrm{onset}})$ describing the minimum of magnetization, and $T_{\mathrm{p}}(<T_1)$, which indicates the maximum of the positive moment [114]. Note here that in some publications, $T_1$ was also called $T_u$. We must note here that these characteristic temperatures are very important for the understanding what is going on in the sample when cooling or warming it in applied magnetic fields.

Figure 7. High-field measurements of the superconducting transition performed in Tokyo (sample Nb002) using a 7T-XL-SQUID [134]. The data were measured in FC-C (field-cooled cooling, filled symbols) and FC-W (field-cooled warming, open symbols) with a constant temperature sweep rate ($|\mathrm{d}T/\mathrm{d}t|=$ 0.01 K/min). $m\left(T\right)$ is always negative, but we must note here the characteristic steps on the FC-W curves indicating the PME.

Figure 7. High-field measurements of the superconducting transition performed in Tokyo (sample Nb002) using a 7T-XL-SQUID [134]. The data were measured in FC-C (field-cooled cooling, filled symbols) and FC-W (field-cooled warming, open symbols) with a constant temperature sweep rate ($|\mathrm{d}T/\mathrm{d}t|=$ 0.01 K/min). $m\left(T\right)$ is always negative, but we must note here the characteristic steps on the FC-W curves indicating the PME.

Figure 5a presents details of $m\left(T\right)$ transitions measured on a punched Nb disk. The superconducting transitions were measured in small applied magnetic fields (10, 50, 100, 200 $\mu$T) perpendicular to the sample surface generated by the Cu coil (using the low-field option with stationary sample). The temperature was continuously swept with a rate of $|\mathrm{d}T/\mathrm{d}t|=$ 38 mK/min. The arrows indicate the direction of the measurement (FC-C and FC-W). The temperature $T_p$ is defined here as the temperature of the maximum $m\left(T\right)$. The inset to (a) shows the definition of the temperature $T_1$ as the lowest $m\left(T\right)$ recorded on the diamagnetic side.

Figure 5b presents a similar situation, but here the measurement is performed at a fixed field ($B_{\mathrm{ext}}=$ 0.5 mT) and the temperature was swept with a rate of $|\mathrm{d}T/\mathrm{d}t|=$ mK/min to reach various minimum values ($T_{\min }$) between $T_1$ and $T_p$ and also slightly below $T_p$, which are indicated in the graph. The inset to (b) gives more details close to $T_1$. Here, one can see that the $m\left(T\right)$ curves are nearly reversible in the temperature range between $T_1$ and $T_c$. Whatever the origin of the paramagnetic moment appearing in the sample between $T_1$ and $T_p$ is, it appears and disappears nearly reversibly with increasing/decreasing the temperature. Furthermore, the onset of the nearly reversible diamagnetic moment can be determined to be at about $T=$ 9.27 K. This moment is fully reversible as long as temperature did not go close to 9.13 K and below. If the sample was cooled below 9.13 K, one can observe a very slight hysteresis of the $m\left(T\right)$ curves even in the temperature range above $T_1$. The $m\left(T\right)$ curves below $T_1$ are fully reversible as long as the temperature $T_{\min }$ is not below about 9.07 K during the cooling and warming cycle. For the $m\left(T\right)$ curves measured at $T_{\min }<$ 9.07 K, one can see during warming a sharper decay of the magnetic moment towards its equilibrium value at $T=T_1$.

Thus, the field-cooled magnetization results for Nb disks show a paramagnetic moment that has a reversible nature as it appears and disappears at the same temperature $T_1$ during cooling and warming, respectively. This moment is superimposed on a typical diamagnetic superconducting behavior below $T_1$ and continues to increase in magnitude until the temperature, $T_{\mathrm{p}}$. Thus, the appearance of a net positive signal at lower temperatures depends on the relative magnitude of the paramagnetic moment of the sample to that of the diamagnetic moment below the temperature $T_{\mathrm{p}}$.

In Figure 6a–c, FC-C and FC-W $m\left(T\right)$-curves are shown in various applied magnetic fields up to 140 mT. A paramagnetic (positive) $m\left(T\right)$ is observed on FC-C for small applied magnetic fields. This positive moment is gradually reducing on increasing field, and the low-T part of each curve is obtained at negative $m\left(T\right)$ for all applied fields above 3 mT. However, the FC-W curves all show the characteristic step in the temperature range 8.8–9.2 K.

Figure 7 presents high-field measurements of the PME on a Nb disk (Nb002) which was carried from Detroit to Tokyo. Using the constant temperature sweep rate of a 7T-XL SQUID [134], the measurements were performed with the superconducting coil in the persistent mode. The measurements were performed after the entire magnetometer had been warmed up to room temperature for servicing. In this way, any spurious trapped fields in the coil system can be safely excluded. From this graph we can see that the $m\left(T\right)$-curves obtained are always on the negative (i.e., diamagnetic) side, but the fingerprints of the PME can be observed as characteristic steps in the FC-W curves up to 200 mT applied magnetic field.

Figure 8. Shifting the PME. The FCC and FCW measurements were perfomed at an applied field of $B_{\mathrm{ext}}=$ 0.05 mT. (a). Temperature range 8.0 $\le T\le$ 9.3 K. The black (FC-C) and red (FC-W) curves are measured, and the green and blue curves are shifted by 13.3 × 10${}^{-9}$ Am${}^2$ as indicated by the magenta arrow. (b) Detail of the superconducting transition around $T_p$.

Figure 8. Shifting the PME. The FCC and FCW measurements were perfomed at an applied field of $B_{\mathrm{ext}}=$ 0.05 mT. (a). Temperature range 8.0 $\le T\le$ 9.3 K. The black (FC-C) and red (FC-W) curves are measured, and the green and blue curves are shifted by 13.3 × 10${}^{-9}$ Am${}^2$ as indicated by the magenta arrow. (b) Detail of the superconducting transition around $T_p$.

Figure 8 gives the results of an important experiment which we called `shifting the PME’. To estimate the magnitude of the paramagnetic step on the FC-C and FC-W curves measured at $B_{\mathrm{ext}}=$ 0.05 mT (see Figure 8a), both the cooling and warming curves below $T_p$ were shifted to such a position that the magnetization curves above $T_1$ and below $T_p$ point toward each other. The best results at this value of $B_{\mathrm{ext}}$ were obtained for the shift by $m_{\mathrm{shift}}=$ 1.33 × 1$0^{-9}$ Am${}^2$. In the detailed view of the transition given in Figure 8b, one can see that the shifted curves combined with the curves above $T_1$ form a nice, archetypal FC-C and FC-W curve. This is a clear indication that the relative shape of the recorded FC-C and FC-W curves below $T_p$ follows an archetypal shape. The crucial change in the superconducting state takes place between temperatures $T_1$ and $T_p$, where an additional positive moment (superconducting currents) appears in the sample, and this moment stays constant in the sample as long as the temperature stays below $T_p$. It again starts to disappear from the sample when the temperature is raised above $T_p$ and it finally disappears completely above $T_1$.

Below $T_{c,\mathrm{onset}}$, $m\left(T\right)$ becomes more negative upon cooling until $T_1$ is reached (≈ 9.16 K at the lowest fields), where $m\left(T\right)$ abruptly turns towards positive values. This increase in $m\left(T\right)$ continues until another characteristic temperature, $T_{\mathrm{p}}$ (≈ 9.16 K at the lowest fields), is reached, where $m\left(T\right)$ exhibits a cusplike behavior. Below $T_{\mathrm{p}}$, the relative temperature dependence of $m\left(T\right)$ appears to correspond to the archetypal FC-C behavior of a superconducting sample not exhibiting the PME. As discussed in Ref. [25], another characteristic feature of the PME for the Nb disks is the large hysteresis between the FC-C and FC-W curves with the FCW curves being lower than the FC-C curves. Upon warming, the $m\left(T\right)$ curves remain practically constant until the moment turns abruptly towards negative values at a temperature essentially the same as $T_{\mathrm{p}}$. Then, at a temperature identical to $T_1$, $m\left(T\right)$ jumps to a less diamagnetic and more probable equilibrium value as the PME appears to vanish suddenly. The similarity in characteristic temperatures where the positive moment first appears during cooling and then disappears during warming as well as where the positive contribution stops increasing in magnitude during cooling and subsequently begins to decrease upon warming suggests that the PME has a reversible nature.

Figure 9. Phase diagram for the PME in bulk Nb disks, constructed using the characteristic temperatures $T_1$, $T_p$ and $T_{c,\mathrm{onset}}$. $T_1$ and $T_p$ are taken from both the warming (`w’) and cooling (`c’) data. Also given are the data of $T_c$ from Ref. [136] for pure and N${}_2$-treated Nb samples. The inset shows a schematic phase diagram including surface superconductivity as described by $H_{c3}\left(T\right)$ and the flux flow region described by the irreversibility field $H_{\mathrm{irr}}\left(T\right)$. The green arrow indicates where FC-C and FC-W measurements are crossing the phase diagram.

Figure 9. Phase diagram for the PME in bulk Nb disks, constructed using the characteristic temperatures $T_1$, $T_p$ and $T_{c,\mathrm{onset}}$. $T_1$ and $T_p$ are taken from both the warming (`w’) and cooling (`c’) data. Also given are the data of $T_c$ from Ref. [136] for pure and N${}_2$-treated Nb samples. The inset shows a schematic phase diagram including surface superconductivity as described by $H_{c3}\left(T\right)$ and the flux flow region described by the irreversibility field $H_{\mathrm{irr}}\left(T\right)$. The green arrow indicates where FC-C and FC-W measurements are crossing the phase diagram.

Figure 9 presents the phase diagram of the PME in the bulk Nb disks, constructed from the temperature variation of the characteristic temperatures $T_1$, $T_p$, and $T_{c,\mathrm{onset}}$. The inset to Figure 9 presents a schematic phase diagram including surface superconductivity as described by $H_{c3}\left(T\right)$ and the flux flow region described by the irreversibility field $H_{\mathrm{irr}}\left(T\right)$. The green arrow indicates where FC-C and FC-W measurements are crossing the phase diagram. $H_{\mathrm{irr}}\left(T\right)$ is for most metallic superconductors very close to $H_{c2}\left(T\right)$ [137]. Note also that in the field-cooling experiments with a magnetic field applied, there is always magnetic flux in the sample, and a pure Meissner state will not be reached even if flux is expelled from the sample. The temperature $T_{c,\mathrm{onset}}$, which is slightly larger as the bulk $T_c$, defines the first onset of superconductivity, i.e., the first recording of a diamagnetic moment which occurs at ≈ 9.23 K for the sample discussed in here. All Nb samples from the same Nb sheet we studied in Detroit, Tokyo and Nancy have $T_c$ between 9.23 and 9.27 K. Also given are $T_c$ data (magnetically measured to determine $H_{c2}$) for pure Nb and Nb treated in N${}_2$ from Ref. [136]. Any differences determined between the FC-C and FC-W runs for these temperatures are within the size of the data points and are the result of a temperature lag between the sample and the thermometer during the cooling and warming processes. One further can note here that the field dependence for all three temperatures is nearly linear: $\mathrm{d}{T}_p/\mathrm{d}{B}_e=$ 13.5 K/T (< 60 mT) and 11 K/T (>60 mT), $\mathrm{d}{T}_1/\mathrm{d}{B}_e=$ 10 K/T, and $\mathrm{d}{T}_{c,\mathrm{onset}}/\mathrm{d}{B}_e=$ 8.7 K/T. Our $T_{c,\mathrm{onset}}$-data are higher and $\mathrm{d}{T}_c=\mathrm{d}{B}_e$ smaller as compared to Weber and Schachinger [136], which may be possible due to different accuracy in measurement/determination of the onset of the diamagnetic signal. However, another explanation is given in Ref. [37]: Our $T_{c,\mathrm{onset}}$ could directly correspond to $H_{c3}\left(T\right)$, i.e., the onset of the surface superconductivity. Then, $T_1$ could correspond to the curve of $H_{c2}\left(T\right)$ and $T_p$ to $H_{\mathrm{irr}}\left(T\right)$, which requires some further analysis using also AC susceptibility measurements (see Section 3.6 below).

Figure 10. PME on Nb disks with perpendicular or parallel magnetic field. (a). $M/H$ recorded in ZFC and FC modes with the magnetic field applied parallel (□) and perpendicular (•) to the Nb disk. The dashed vertical lines indicate the temperatures $T_u\le T_1$ and $T_p$, see text. Reprinted with permission from Ref. [116]. (b). PME on a Nb disk with the applied magnetic field parallel to the sample surface, measured in the year 2023 in Nancy using a QD PPMS-VSM system [134]. The lines serve as guides for the eye.

Figure 10. PME on Nb disks with perpendicular or parallel magnetic field. (a). $M/H$ recorded in ZFC and FC modes with the magnetic field applied parallel (□) and perpendicular (•) to the Nb disk. The dashed vertical lines indicate the temperatures $T_u\le T_1$ and $T_p$, see text. Reprinted with permission from Ref. [116]. (b). PME on a Nb disk with the applied magnetic field parallel to the sample surface, measured in the year 2023 in Nancy using a QD PPMS-VSM system [134]. The lines serve as guides for the eye.

In Figure 10a,b the results of applying a magnetic field parallel to the sample surface are shown. Figure 10a, presenting $M/H_{\perp }\left(T\right)$ and $M/H_{\Vert }\left(T\right)$, indicates the temperatures $T_u$ (which is defined as the first appearance of a paramagnetic moment, and $T_u\le T_1$ as discussed previously) and $T_p$, where the positive contribution stops increasing in magnitude during cooling [116]. The values of the applied field were, however, not given in [116]. It is also evident from Figure 10a that these temperatures can be identified with certain characteristic features in the ZFC data. $T_p$ can be associated with the temperature where the diamagnetic response is at its maximum value and full flux exclusion occurs, while $T_u$ represents the temperature where global diamagnetic screening disappears during warming. On the other hand, the FC $M/H$-data with in-plane field (□) exhibit a more complex but completely diamagnetic behavior, including a hysteresis depending upon whether the sample is being cooled or subsequently warmed through the superconducting transition.

Figure 10b presents QD PPMS-VSM [134] measurements performed in Nancy on a rectangular Nb disk stemming from sheet DS4D with the magnetic field applied parallel to the sample surface. Fields in the range between 1 mT and 100 mT were applied. For fields up to 10 mT applied parallel to the sample surface, we observe a positive (paramagnetic) response, which changes into completely diamagnetic signals on further increase of the applied field. Note here also the shift of $T_c$ towards lower values with increasing the applied field. This observation clearly points out that PME is possible also in the configuration $H\Vert$ sample surface.

3.3. Magnetization loops close to the superconducting transition

In order to gain more information about the physical origin of this additional paramagnetic moment, we performed detailed magnetization hysteresis loop (MHL) measurements in three distinct temperature ranges. MHLs of samples exhibiting the PME were rarely investigated in literature on both Nb and HTSc materials. Kötzler et al. [22] showed some virgin magnetization curves of their Bi-2212 samples, and Thompson et al. [31] have presented a MHL on Nb. The MHL presented in Ref. [31] showed a quite specific nearly parallelogram-like shape but there was no detailed analysis nor discussion of this feature. Thus, we take here the opportunity to present a detailed experimental analysis of the MHLs measured on Nb samples exhibiting the PME and a correlation of these results to the widely used PME measurements of magnetic moment at constant magnetic field while the temperature changes.

Figure 11a shows MHLs measured in Detroit on one of the Nb disk samples at temperatures between 8.96 and 9.08 K. These are "archetypal" MHLs of a type II superconductor with the shape given by the field-dependent superconducting currents induced in the sample and vortex pinning in this material. Note here the well-developed central peak located at slightly negative values, but close to zero field as it is expected from a bulk, superconducting sample [138,139]. Also shown are the corresponding virgin curves (i.e., the magnetization curves measured when the magnetic field was first applied to the sample after cooling in zero field). The joining of the virgin curve with the main MHL is marked as "A”. All the MHLs presented in Figure 11a were measured in the standard operation mode of the QD MPMS SQUID magnetometer with scan length below 1 cm. In contrast, the MHLs in the transition region between 9.00 K and 9.20 K were measured with temperature steps of 0.01 K using the stationary sample technique. At at field of ∼1 mT, there is still a finite induced magnetic moment and when the direction of the field ramping is reversed, one obtains the so-called "reverse leg" of the MHL given by the process of reversing the induced currents in the sample. This process is qualitatively similar to the process when the virgin curve merges the full MHL.

Figure 11b shows MHLs taken at elevated temperatures in the range 9.05 to 9.10 K, i. e., around the characteristic temperature, $T_{\mathrm{p}}$. While the MHLs measured at 9.00 K and 9.04 K look again more like "archetypal" MHLs, the MHL measured at 9.08 K has apparently a different shape with no clear maximum near to zero field. Even for the MHLs measured at 9.00 K and 9.04 K, one should note that the virgin curves are straight with a very sharp turn when they merge the full MHL (see the area marked as "B" in Figure 11b). All these curves develop a more parallelogram-like shape without any low-field maximum. Note also that the slope of the virgin curve changes between 9.05 K and 9.06 K. There is furthermore a significant change in the shape of the reverse legs of the MHLs. Along with this change also the slope of the reverse leg changes to being steeper at temperatures below 9.05 K (see also the analysis shown in Figure 13 below).

Figure 11. Magnetic measurements performed in Detroit on Nb disks with $H\perp$ sample surface. (a). MHLs on the Nb disk sample in the temperature range 8.96 $\le T\le$ 9.08 K. All MHLs exhibit the archetypal shape of a classical superconductor as found in the textbooks with a central peak close to 0 field, but at slightly negative values. (b). MHLs on the Nb disk sample close to $T_c$ in the temperature range 9.05 $\le T\le$ 9.10 K. The central peak is still visible in the 9.05 K run, but at the higher temperatures, this peak vanishes and the MHL assumes a parallogram-like shape. The areas marked ”A” and ”B” indicate the merging of the virgin curve with the main MHL.

Figure 11. Magnetic measurements performed in Detroit on Nb disks with $H\perp$ sample surface. (a). MHLs on the Nb disk sample in the temperature range 8.96 $\le T\le$ 9.08 K. All MHLs exhibit the archetypal shape of a classical superconductor as found in the textbooks with a central peak close to 0 field, but at slightly negative values. (b). MHLs on the Nb disk sample close to $T_c$ in the temperature range 9.05 $\le T\le$ 9.10 K. The central peak is still visible in the 9.05 K run, but at the higher temperatures, this peak vanishes and the MHL assumes a parallogram-like shape. The areas marked ”A” and ”B” indicate the merging of the virgin curve with the main MHL.

Below $T_p$, the MHL increases significantly and acquires an archetypal shape of MHL loop of a bulk superconductor with maximum close to $B_{\mathrm{ext}}\approx$ 0.

Figure 12a shows MHLs in the very interesting temperature range between 9.07 and 9.14 K, i.e., between $T_1\approx$ 9.16 K and $T_{\mathrm{p}}\approx$ 9.05 K. MHLs at these temperatures are found to exhibit several distinct features that probably have the same physical origin as the appearance of the paramagnetic moment during field-cooling in small applied fields. The MHLs have the shape of a nearly regular parallelogram with all turning points being sharp. Note that the reverse legs are entirely linear, all the turning points are quite sharp, and the size of the parallelograms increases with decreasing temperature. Also, the shape of the initial magnetization curve (virgin curve, abbreviated VC) is very linear and then abruptly merges with the nearly field-independent MHL (see Figure 12b). These features cannot be explained by magnetic flux gradually penetrating the superconducting sample, governed by vortex pinning when the field is changed.

Figure 12. Further details on the MHLs measured close to $T_c$. (a). MHLs in the temperature range 9.07 $\le T\le$ 9.14 K. (b). The virgin curves (VCs) of the MHLs in the temperature range 9.07 $\le T\le$ 9.14 K. The VCs are linear and join the MHLs quite abruptly. (c). The reverse legs of the MHLs 9.05 $\le T\le$ 9.12 K. All reverse legs are linear and the ends are quite sharp, i.e., hardly rounded off.

Figure 12. Further details on the MHLs measured close to $T_c$. (a). MHLs in the temperature range 9.07 $\le T\le$ 9.14 K. (b). The virgin curves (VCs) of the MHLs in the temperature range 9.07 $\le T\le$ 9.14 K. The VCs are linear and join the MHLs quite abruptly. (c). The reverse legs of the MHLs 9.05 $\le T\le$ 9.12 K. All reverse legs are linear and the ends are quite sharp, i.e., hardly rounded off.

Here it is important to mention again that all MHLs at temperatures close to the transition temperature were determined from the SQUID voltage change generated by stationary sample. This method is very "safe" as it eliminates spurious signals that may be generated when sample is moving during the measurement. However, this method cannot be used at higher fields and consequently at lower temperatures where the induced moments are large and we cannot measure anything but reversible screening currents. Fortunately, at lower temperatures we can use the conventional measurement of the magnetic moments in the point by point method with the sample moving (the scan length should be as short as possible) over a distance in a magnetic field generated by the build-in superconducting magnet. At lower temperatures the induced magnetic moment is quite large and so, the possible spurious signals due to moment motion are relatively small.

Figure 12b shows more details of the virgin curves of the MHLs measured after cooling down in zero field. The slope $S=\mathrm{d}m/\mathrm{d}{H}_{\mathrm{ext}}$ of virgin curves recorded at $T=$ 9.06 K and above is remarkably lower (by about 20 %) as compared to the slope of all virgin curves recorded at $T=$ 9.05 K and below. The major change of the virgin curve slope takes place just below $T_{\mathrm{p}}$ where also a remarkable change in the shape of the MHLs takes place. Additionally, the slope S of the initial curves changes below $T_{\mathrm{p}}$ with the magnitude and temperature dependence of this change corresponding to the step observed in the zero field-cooled susceptibility curves [25]. At the temperature $T_{\mathrm{p}}$ also the VC shape changes. Below $T_p$, the VC bends when approaching the MHL indicating gradual penetration of magnetic flux into the sample.

Finally, Figure 12c illustrates the field reversal on the MHLs at temperatures from 9.05 to 9.12 K. In this temperature range, one can see very straight reversal legs with very sharp and regular turning points at the MHL at field reversal. This behavior is again a very important characteristic feature of the bulk Nb disks, closely related to the presence of the PME.

Figure 13. Evaluated details of the hysteresis measurements. The graph gives the MHL magnitude (maximum induced magnetic moment) as a function of temperature. The blue datapoints (•) give the data obtained from the MHLs, the black crosses (+) represent the data from a second run. The slope from the archtypal MHLs as shown in the inset () and the slope of the component C in the main panel () are the same. It is obvious from this graph that at $T_p$ an abrupt change in the MHL shape takes place, and the normal flux pinning vanishes. At $T>$ 9.06 K, the component P is measured follwing a completely different slope ().

Figure 13. Evaluated details of the hysteresis measurements. The graph gives the MHL magnitude (maximum induced magnetic moment) as a function of temperature. The blue datapoints (•) give the data obtained from the MHLs, the black crosses (+) represent the data from a second run. The slope from the archtypal MHLs as shown in the inset () and the slope of the component C in the main panel () are the same. It is obvious from this graph that at $T_p$ an abrupt change in the MHL shape takes place, and the normal flux pinning vanishes. At $T>$ 9.06 K, the component P is measured follwing a completely different slope ().

Figure 13 shows the temperature dependence of the magnitude of MHL (i.e., the maximum induced magnetic moment, $m_{\max }\left(T\right)$). $m_{\max }\left(T\right)$ is nearly linear below the temperature $\approx T_p$ going sharply towards zero at about 9.065 K, as indicated by dashed line (). The inset to Figure 13 presents the same analysis for the temperature range 8.7 $\le T\le$ 9.0 K, i.e., the range where the "normal" MHL shape is found. The slope obtained here and the slope of the magenta dashed line in the main panel are the same. However, above 9.06 K, $m_{\max }\left(T\right)$ abruptly changes the slope and decreases, again nearly linearly, but with a slope being about one order of magnitude smaller, as indicated by the dashed green line (). Thus, in the temperature range $T_p\le T_c$, the PME-MHLs are visible, giving an indication of the giant vortex state.

It is obvious from this graph that the $m_{\max }\left(T\right)$ dependence can be formally separated into two components, one (we will call this component "C") that goes sharply to zero at $T=$ 9.06 K $\approx T_p$, and another component (we will call this component "P") that has a much weaker temperature dependence. The component P is not "visible" at temperatures below $T_p$, where the P component is overwhelmed by the larger C component and the magnetic moment is given primarily by the dominant component C, which describes the classic situation of flux pinning of Abrikosov vortices. The situation changes below the characteristic temperature, $T_p$, where the magnetic moment from the component C is (practically) zero and the $m_{\max }\left(T\right)$-dependence is entierly given by the component P that diminishes only at temperatures close to $T_1$ or higher.

Considering both the shape and character of MHLs at various temperatures, and also the FC and ZFC curves studied in detail in Refs. [25,114,115], we can attribute the component C to the conventional behavior of a type-II superconductor, where induced currents are governed primarily by vortex pinning. The origin of the component P is still not fully understood. This component is obvious only above $T_p$, where the C component diminishes to zero, but the character of the $m_{\max }\left(T\right)$-dependence indicates that the P component is present in the sample also at temperatures below $T_p$. We thus believe that the component P of the induced magnetic moment is responsible for specific superconducting behavior of Niobium below the transition temperature including (but not limited to) the appearance of that positive magnetic moment when the sample is cooled in small applied magnetic fields (i.e., the Paramagnetic Meissner effect).

Figure 14. Abrading the surface of the Nb disks. Two samples punched from the same Nb sheet were studied, Nb1 left as is, and Nb2 was mechanically abraded on both top and bottom surface (the sample amount was reduced by 10 %). (a). FCC and FCW curves in an applied field of 2 mT. Sample Nb1 (as-prepared, ), and sample Nb2 (abraded, ). (b). Details around $T_c$ of the data shown in (a). (c). FCC and FCW curves in an applied field of 20 mT. (d). FCC and FCW curves in an applied field of 60 mT. The abraded sample does not show any feature of the PME at any temperature/field as compared to the as-prepared sample Nb1.

Figure 14. Abrading the surface of the Nb disks. Two samples punched from the same Nb sheet were studied, Nb1 left as is, and Nb2 was mechanically abraded on both top and bottom surface (the sample amount was reduced by 10 %). (a). FCC and FCW curves in an applied field of 2 mT. Sample Nb1 (as-prepared, ), and sample Nb2 (abraded, ). (b). Details around $T_c$ of the data shown in (a). (c). FCC and FCW curves in an applied field of 20 mT. (d). FCC and FCW curves in an applied field of 60 mT. The abraded sample does not show any feature of the PME at any temperature/field as compared to the as-prepared sample Nb1.

Figure 15. Ion implanting in Nb disks. (a). The zero-field-cooled lower and field-cooled-warming upper susceptibility data for an untreated Nb disk (punched from a 0.25-mm thick Nb sheet) with magnetic fields applied normal to the disk surface. (b). The hysteretic behavior between the field-cooled-cooling (solid symbols) and field-cooled-warming (open symbols) susceptibility data for an untreated Nb disk (circles) and an ion-implanted Nb disk (triangles) for a 50 $\mu$T (500 mOe) field applied normal to the surface of the disk. Figure reproduced with permission from Ref. [32].

Figure 15. Ion implanting in Nb disks. (a). The zero-field-cooled lower and field-cooled-warming upper susceptibility data for an untreated Nb disk (punched from a 0.25-mm thick Nb sheet) with magnetic fields applied normal to the disk surface. (b). The hysteretic behavior between the field-cooled-cooling (solid symbols) and field-cooled-warming (open symbols) susceptibility data for an untreated Nb disk (circles) and an ion-implanted Nb disk (triangles) for a 50 $\mu$T (500 mOe) field applied normal to the surface of the disk. Figure reproduced with permission from Ref. [32].

3.4. Manipulating the PME

To investigate the influence of the sample surfaces on the PME, several experiments were performed at Detroit: (i) the surfaces of the Nb disks were abraded (thereby the sample thickness was reduced by about 10%), and (ii) the sample edges were treated using sandpaper. Sanding off the edges of the sample did not lead to a change of the PME characteristics, so these data are not shown here. In contrast, abrading the sample surface (sample Nb2) was found to have a significant effect on the PME of the Nb disks as illustrated in Figure 14a–d. DC magnetic fields of 2 mT (a,b), 20 mT (c) and 60 T (d) were applied. The as-prepared sample (red datapoints, sample Nb1) exhibits all the features of the PME as discussed before, whereas the abraded sample does not show any signature of the PME at any applied field. Note also when defining $T_{c,\mathrm{onset}}$ as the temperature of the onset of a diamagnetic moment on the cooling curve (FC-C) and disappearance of the moment on the warming curve (FC-W), the abraded sample Nb2 exhibits a $T_{c,\mathrm{onset}}$, which is about 0.05 K higher than that of the Nb disk with PME (sample Nb1).

Figure 16. FC-C and FC-W measurements of $m\left(T\right)$ performed using the same sample (Nb002) in 3 places on Earth with more than 20 years difference between the experiments. (a). Original measurement in Detroit, 1997. SQUID with stationary sample. (b). Measurement performed at SRL/ISTEC, Tokyo, 1999, using a 5T-SQUID with ultra-low field option. (c). Measurement performed at IJL Nancy, 2019, using an MPMS3 SQUID system with small scan length. (d). Comparison of the Detroit and Nancy data concerning the characteristic temperatures $T_1$, $T_p$, and $T_{c\mathrm{FC}}$ (i.e., $T_c$ obtained from FC data).

Figure 16. FC-C and FC-W measurements of $m\left(T\right)$ performed using the same sample (Nb002) in 3 places on Earth with more than 20 years difference between the experiments. (a). Original measurement in Detroit, 1997. SQUID with stationary sample. (b). Measurement performed at SRL/ISTEC, Tokyo, 1999, using a 5T-SQUID with ultra-low field option. (c). Measurement performed at IJL Nancy, 2019, using an MPMS3 SQUID system with small scan length. (d). Comparison of the Detroit and Nancy data concerning the characteristic temperatures $T_1$, $T_p$, and $T_{c\mathrm{FC}}$ (i.e., $T_c$ obtained from FC data).

Thompson et al. [32] demonstrated that ion implantation into the sample surface area can create the PME in a sample which did not show the PME prior to irradiation. Since these Nb superconducting samples exhibiting the PME have a surface microstructure containing defects, which are known to increase the critical current density, it is reasonable to expect that introducing defects through ion implantation, e.g., might enhance or even create the PME in other Nb disks. For the Kr-ion bombardment, disks of 6.4-mm diameter were punched from an untreated, cold-rolled, 0.25-mm thick sheet of niobium (99.8% purity, Johnson-Matthey) as well as from a 6.45 cm${}^2$ (1 in${}^2$) section of the same sheet that had both sides ion implanted with 200 keV Kr ions at a dose of 6×10${}^{16}$/cm${}^2$. During the following magnetic measurements in the SQUID system in Detroit, the samples were kept stationary. The result of this procedure is presented in Figure 15a,b. From these figures, it is very clear that the PME can be induced in Nb disks by implanting Kr ions to a depth of about 120 nm below the surfaces of the disks. Enhancing the $T_c$ variation and the effective pinning strength from existing surface defects which result from the ion bombardment are important factors in the development of the PME. By creating a surface defect structure with greater relative depth into the thicker Nb disks, these lower-$T_c$ regions serve as more effective pinning sites which produce inhomogeneous field variations whose temperature dependences could result in the PME characteristic behavior. In order to further our understanding of the effect that the ion implanting has upon the magnetization characteristics, one should note that the Kr ions penetrate uniformly to a depth of 40 nm below the surface and then the concentration drops off to a negligible value beyond 120 nm. Thus the observed magnetic behavior is strongly affected by just the first 120 nm below the two surfaces of the disks. Clearly the ion bombardment has created an inhomogeneous superconducting sample with a $T_c$ variation as evidenced by the appearance of a second diamagnetic transition at 9.07 K. It is known, e.g., that the $T_c$ of Nb is easily reduced by oxidation and strains. Furthermore, Halbritter [140] has shown that an enhanced oxidation is promoted around defects and serrations on the Nb surfaces so that the defect regions can extend down to several microns below the surface. Consequently, it is plausible that the Kr ions have the greatest impact on these regions by reducing the $T_c$ and extending their depth below the surface. Secondly, the ion implanting has produced sites with extremely strong flux pinning as indicated by the narrowing of the ZFC $M/H$ transition width of the largest diamagnetic change. The inducing of PME through ion implantation on a sample which previously did not exhibit PME signatures, helps further the understanding of PME.

3.6. AC susceptibility measurements on Nb disks

The PME was observed using AC susceptibility on HTSc Bi-2212 [16,24], and much later by Ge et al. [37] on ZrB${}_{12}$ crystals. The signatures, which indicate the presence of PME, are completely different for the HTSc and the conventional ones, as for the HTSc PME is revealed by a strong frequency dependence on the left side of the loss peak in ${\chi }^{\prime \prime }$ (measured frequencies, $f=$ 17 mHz up to 1.7 kHz) as well as a dependence on the AC field amplitudes ($h_{\mathrm{ac}}=$ 0.4 $\mu$T – 12 $\mu$T), showing a linear response [24]. For effects of flux creep, the higher harmonics were analyzed in [16]. In the case of ZrB${}_{12}$ [37], an anomalous positive peak is seen in the ${\chi }^{\prime }$-data ($f=$ 333 Hz, $h_{\mathrm{ac}}=$ 0.1 mT), and no frequency dependence of the loss peak in ${\chi }^{\prime \prime }$ was reported. The positive peak in ${\chi }^{\prime }$ was termed diffraction paramagnetic effect (DPE), and enabled the determination of $T_c^{\mathrm{surface}}$ as well as the onset of diamagnetic response, $T_{\mathrm{irr}}$ (see also Figure 23 below).

Measurements of the AC susceptibility were performed in Nancy using the AC-option of the MPMS3 SQUID system [134] to obtain further information on the details of the superconducting transition of the Nb disks from Detroit (see Figure 17a–d). These experiments were done after ensuring the PME effect in the Nb disks by SQUID measurements. Figure 17a gives the recorded superconducting transition recorded in a DC field of 1 mT for frequencies of 1, 10, 100 and 1000 Hz. The AC amplitude was chosen to be 0.1 mT (green curves) and 1 mT (orange curves). There is only a weak frequency dependence at the loss peak on the right side (decreasing T), but the blue arrow marks a secondary loss peak when warming up the sample. The inset depicts the situation for an applied DC field of 1 mT, AC amplitude of 1 mT and frequency of 1 Hz. Given are the real (${\chi }^{\prime }$, ) and the imaginary part (${\chi }^{\prime \prime }$, ). Both cooling and warming curves are represented. A tiny positive signal is obtained for ${\chi }^{\prime }$, similar to the case of ZrB${}_{12}$. Figure 17b shows the same experiments but with an applied DC field of 2 mT, Figure 17c for an applied DC field of 5 mT and Figure 17d for an applied DC field of 10 mT. Thus, traces of PME in Nb can only be observed at low frequencies (1 Hz) and small applied DC fields (1 mT) and AC amplitudes (1 mT). As the warming (72 mK/min) /cooling (30 mK/min) experiments were done with different temperature sweep rates, this may be a reason for the shift of the loss peak towards higher temperatures, but the different shape of peak and the kinks do correspond well to the DC $m\left(T\right)$ measurements. These observations demonstrate the presence of PME signatures also in the AC susceptibility measurements, and the signatures are present in both the real and imaginary part of the susceptibility.

Figure 17. AC measurements on an Nb disk performed at IJL Nancy. The AC frequencies were varied between 1, 10, 100 and 1000 Hz, and two AC amplitudes of 0.1 mT () and 1 mT () were applied. (a). Measurement with an applied DC field of 1 mT. The blue arrow points to a secondary loss peak when warming up. The inset presents the superconducting transition for 1 Hz, DC field 1 mT, AC amplitude 1 mT. The imaginary part, ${\chi }^{\prime \prime }$, is given by , and the real part ${\chi }^{\prime }$ by . The magenta arrow indicates a tiny positive signal in ${\chi }^{\prime }$. (b). Measurement with an applied DC field of 2 mT. (c). Measurement with an applied DC field of 5 mT. (d). Measurement with an applied DC field of 10 mT.

Figure 17. AC measurements on an Nb disk performed at IJL Nancy. The AC frequencies were varied between 1, 10, 100 and 1000 Hz, and two AC amplitudes of 0.1 mT () and 1 mT () were applied. (a). Measurement with an applied DC field of 1 mT. The blue arrow points to a secondary loss peak when warming up. The inset presents the superconducting transition for 1 Hz, DC field 1 mT, AC amplitude 1 mT. The imaginary part, ${\chi }^{\prime \prime }$, is given by , and the real part ${\chi }^{\prime }$ by . The magenta arrow indicates a tiny positive signal in ${\chi }^{\prime }$. (b). Measurement with an applied DC field of 2 mT. (c). Measurement with an applied DC field of 5 mT. (d). Measurement with an applied DC field of 10 mT.

4. Magnetic Imaging

Figure 18. Scanning SQUID microscope images. (a–f) present images of a granular Bi-2212 sample, cooled and imaged in various applied magnetic fields. Each image comprises 512 × 512 pixels, and each pixel represents a distance of 6 $\mu$m. The individual images are labelled by the cooling field, and by the maximal range of variation of the flux (in units of the flux quantum, ${\mathsf{\Phi }}_0$) in each case. The small rectangles indicate where profiles were taken in Ref. [104], which are not shown here. All images were taken at $T=$ 4.2 K. (a). Cooling field 1 $\mu$T (0.01 G), 0.21 ${\mathsf{\Phi }}_0$. (b). Cooling field 3 $\mu$T (0.03 G), 0.21 ${\mathsf{\Phi }}_0$. (c). Cooling field 10 $\mu$T (0.1 G), 0.21 ${\mathsf{\Phi }}_0$. (d). Cooling field 30 $\mu$T (0.3 G), 0.39 ${\mathsf{\Phi }}_0$. (e). Cooling field 100 $\mu$T (1 G), 1.65 ${\mathsf{\Phi }}_0$. (f). Cooling field 300 $\mu$T (3 G), 7.6 ${\mathsf{\Phi }}_0$. (g)–(h) give images obtained on a Nb disk from Detroit at $T=$ 4.2 K. (g). Sample with no PME, applied field of ∼ 1.6 $\mu$T (1.6 mG). (h) sample with strong PME, applied field ∼ 2.8 $\mu$T (2.8 mG). Images (a)–(f) reproduced with permission from Ref. [104], images (g) and (h): Courtesy of J.R. Kirtley.

Figure 18. Scanning SQUID microscope images. (a–f) present images of a granular Bi-2212 sample, cooled and imaged in various applied magnetic fields. Each image comprises 512 × 512 pixels, and each pixel represents a distance of 6 $\mu$m. The individual images are labelled by the cooling field, and by the maximal range of variation of the flux (in units of the flux quantum, ${\mathsf{\Phi }}_0$) in each case. The small rectangles indicate where profiles were taken in Ref. [104], which are not shown here. All images were taken at $T=$ 4.2 K. (a). Cooling field 1 $\mu$T (0.01 G), 0.21 ${\mathsf{\Phi }}_0$. (b). Cooling field 3 $\mu$T (0.03 G), 0.21 ${\mathsf{\Phi }}_0$. (c). Cooling field 10 $\mu$T (0.1 G), 0.21 ${\mathsf{\Phi }}_0$. (d). Cooling field 30 $\mu$T (0.3 G), 0.39 ${\mathsf{\Phi }}_0$. (e). Cooling field 100 $\mu$T (1 G), 1.65 ${\mathsf{\Phi }}_0$. (f). Cooling field 300 $\mu$T (3 G), 7.6 ${\mathsf{\Phi }}_0$. (g)–(h) give images obtained on a Nb disk from Detroit at $T=$ 4.2 K. (g). Sample with no PME, applied field of ∼ 1.6 $\mu$T (1.6 mG). (h) sample with strong PME, applied field ∼ 2.8 $\mu$T (2.8 mG). Images (a)–(f) reproduced with permission from Ref. [104], images (g) and (h): Courtesy of J.R. Kirtley.

Figure 19. MO images obtained at University of Liège of an Nb disk from Detroit. (a). The MO image at $H=$ 5 mT applied field, and the temperature is swept from 10 K to about 8 K. The top L-shape indicates the MO indicator film, the inner L-shape represents the sample edges. The two yellow boxes give the regions ($I_{\mathrm{out}}$, $I_{\mathrm{in}}$), where the profiles are taken for (b). (b). Profiles taken in the two yellow boxes marked in (a). The black curves are for $I_{\mathrm{out}}$, and the red curves for $I_{\mathrm{in}}$.

Figure 19. MO images obtained at University of Liège of an Nb disk from Detroit. (a). The MO image at $H=$ 5 mT applied field, and the temperature is swept from 10 K to about 8 K. The top L-shape indicates the MO indicator film, the inner L-shape represents the sample edges. The two yellow boxes give the regions ($I_{\mathrm{out}}$, $I_{\mathrm{in}}$), where the profiles are taken for (b). (b). Profiles taken in the two yellow boxes marked in (a). The black curves are for $I_{\mathrm{out}}$, and the red curves for $I_{\mathrm{in}}$.

Figure 20. Diamond center imaging by AMES on an Nb sample with PME. (a). Temperature-dependent total magnetic moment measured using Quantum Design MPMS. Shown are ZFC-W and FC-C curves measured in Nb. (b). FC profiles of the magnetic induction for applied magnetic fields of 1.0, 1.2, and 5 mT (10, 12, and 50 Oe) recorded for an Nb disk-shaped crystal. Measurement performed at $T=$ 4.2 K. The signatures of the paramagnetic Meissner effect (PME) are observed in various random regions for low magnetic fields. Cooling in 1 mT (10 Oe, red datapoints) and 1.2 mT (12 Oe, green datapoints) applied magnetic fields results in very similar profiles. The inset to (b) presents a temperature-resolved measurement in a 1 mT (10 Oe) magnetic field upon FC-C. The peak (‘P’) and valley positions (‘V’) of the inset are indicated by arrows in the main panel. Image reproduced with permission from Ref. [150].

Figure 20. Diamond center imaging by AMES on an Nb sample with PME. (a). Temperature-dependent total magnetic moment measured using Quantum Design MPMS. Shown are ZFC-W and FC-C curves measured in Nb. (b). FC profiles of the magnetic induction for applied magnetic fields of 1.0, 1.2, and 5 mT (10, 12, and 50 Oe) recorded for an Nb disk-shaped crystal. Measurement performed at $T=$ 4.2 K. The signatures of the paramagnetic Meissner effect (PME) are observed in various random regions for low magnetic fields. Cooling in 1 mT (10 Oe, red datapoints) and 1.2 mT (12 Oe, green datapoints) applied magnetic fields results in very similar profiles. The inset to (b) presents a temperature-resolved measurement in a 1 mT (10 Oe) magnetic field upon FC-C. The peak (‘P’) and valley positions (‘V’) of the inset are indicated by arrows in the main panel. Image reproduced with permission from Ref. [150].

Figure 21. Average local magnetic field in Au/Ho/Nb trilayers as a function of the muon implantation energy and mean stopping distance. (a). ${\overrightarrow{B}}_{\mathrm{loc}}$ values from single-energy asymmetry fits versus implantation energy (bottom x-axis) and mean stopping distance (top x-axis) in the normal state (•, $T=$ 10 K) and superconducting state (•, $T=$ 5 K). (b). Data showing the inverse Meissner state in Au. The continuous lines are a guide to the eye. (c). Magnetization and screening current profile from the Ho/Nb interface in Au/Ho/Nb. Local magnetic field ${\overrightarrow{B}}_{\mathrm{loc}}\left(z\right)$ determined as global-energy fit of the LE-$\mu$SR measurement data (, left y-axis) and theoretical model (, left y-axis); calculated dimensionless screening current density, $J_x\left(z\right)$ flowing parallel to the x-axis in (a) inside the plane of the thin film heterostructure (gray curve, right side y-axis). Dashed lines show that the position of the maximum in ${\overrightarrow{B}}_{\mathrm{loc}}\left(z\right)$ coincides with that of the null in $J_x\left(z\right)$. Image reproduced with permission from Ref. [56].

Figure 21. Average local magnetic field in Au/Ho/Nb trilayers as a function of the muon implantation energy and mean stopping distance. (a). ${\overrightarrow{B}}_{\mathrm{loc}}$ values from single-energy asymmetry fits versus implantation energy (bottom x-axis) and mean stopping distance (top x-axis) in the normal state (•, $T=$ 10 K) and superconducting state (•, $T=$ 5 K). (b). Data showing the inverse Meissner state in Au. The continuous lines are a guide to the eye. (c). Magnetization and screening current profile from the Ho/Nb interface in Au/Ho/Nb. Local magnetic field ${\overrightarrow{B}}_{\mathrm{loc}}\left(z\right)$ determined as global-energy fit of the LE-$\mu$SR measurement data (, left y-axis) and theoretical model (, left y-axis); calculated dimensionless screening current density, $J_x\left(z\right)$ flowing parallel to the x-axis in (a) inside the plane of the thin film heterostructure (gray curve, right side y-axis). Dashed lines show that the position of the maximum in ${\overrightarrow{B}}_{\mathrm{loc}}\left(z\right)$ coincides with that of the null in $J_x\left(z\right)$. Image reproduced with permission from Ref. [56].

5. Discussion

Figure 22. Magnetic susceptibility, $\chi$, of mesoscopic Al disks, see also Figure 2f. (a). Field dependence of the Meissner response for a Al disk with 1.0 $\mu$m diameter (□) and for one with 2.5 $\mu$m diameter (•). The thickness is for both disks 0.1 $\mu$m. The strongly oscillating behaviour clearly seen (the dashed line is a guide to the eye) for the larger sample is due to size quantization. Each jump corresponds to a change in the number of vortices inside the disk, which can either form an array of single quantum vortices or assemble into a single giant vortex. The inset to (a) compares the field-cooling (FC) and zero-field-cooling (ZFC) magnetization for the 2.5-mm disk at the field where the paramagnetic response is close to its maximum value. The ZFC response is always diamagnetic, and the jumps in the ZFC curve correspond to entry of individual vortices into the disk interior. (b). Comparison of the magnetization states reached by cooling in a field and by sweeping the field at a constant temperature (arrows) at $T=$ 0.4 K. The field-cooling (FC-C) data shown by □ are for the 2.5-$\mu$m disk shown in (a). The filled boxes (▪) indicate the low-temperature states as shown in the inset to (a), ZFC and FC. The inset to (b) illustrates the compression of a giant vortex (T close but below $T_c$) into a smaller volume (T further away from $T_c$,) which enables extra flux to enter the sample at the surface. Image reproduced with permission from Ref. [63].

Figure 22. Magnetic susceptibility, $\chi$, of mesoscopic Al disks, see also Figure 2f. (a). Field dependence of the Meissner response for a Al disk with 1.0 $\mu$m diameter (□) and for one with 2.5 $\mu$m diameter (•). The thickness is for both disks 0.1 $\mu$m. The strongly oscillating behaviour clearly seen (the dashed line is a guide to the eye) for the larger sample is due to size quantization. Each jump corresponds to a change in the number of vortices inside the disk, which can either form an array of single quantum vortices or assemble into a single giant vortex. The inset to (a) compares the field-cooling (FC) and zero-field-cooling (ZFC) magnetization for the 2.5-mm disk at the field where the paramagnetic response is close to its maximum value. The ZFC response is always diamagnetic, and the jumps in the ZFC curve correspond to entry of individual vortices into the disk interior. (b). Comparison of the magnetization states reached by cooling in a field and by sweeping the field at a constant temperature (arrows) at $T=$ 0.4 K. The field-cooling (FC-C) data shown by □ are for the 2.5-$\mu$m disk shown in (a). The filled boxes (▪) indicate the low-temperature states as shown in the inset to (a), ZFC and FC. The inset to (b) illustrates the compression of a giant vortex (T close but below $T_c$) into a smaller volume (T further away from $T_c$,) which enables extra flux to enter the sample at the surface. Image reproduced with permission from Ref. [63].

Figure 23. (a). Temperature dependence of the magnetization in the FFCW mode at 0.5 mT (5 Oe). (b). Phase diagramfor the PME in FFCW mode. The third critical field $H_{c3}$ is defined from the onset of DPE in the in-phase ac susceptibility measurements; $H_{c2}$ is defined from the intersection of two linear fits of the $M\left(T\right)$ curves above and below the onset; $T_{irr}$ is derived as the onset of a diamagnetic signal on the in-phase ac susceptibility curve.The solid and dashed lines are plots of the empirical formula $H\left(T\right)=H_0{[1-{(T/T_c)}^2]}^n$ The crosses show the field locations where the magnetic relaxation curves are measured. Image reproduced with permission from Ref. [37].

Figure 23. (a). Temperature dependence of the magnetization in the FFCW mode at 0.5 mT (5 Oe). (b). Phase diagramfor the PME in FFCW mode. The third critical field $H_{c3}$ is defined from the onset of DPE in the in-phase ac susceptibility measurements; $H_{c2}$ is defined from the intersection of two linear fits of the $M\left(T\right)$ curves above and below the onset; $T_{irr}$ is derived as the onset of a diamagnetic signal on the in-phase ac susceptibility curve.The solid and dashed lines are plots of the empirical formula $H\left(T\right)=H_0{[1-{(T/T_c)}^2]}^n$ The crosses show the field locations where the magnetic relaxation curves are measured. Image reproduced with permission from Ref. [37].

6. Conclusions and outlook

References

1. Meissner, W.; Ochsenfeld, R. Ein neuer Effekt bei Eintritt der Supraleitfähigkeit. Naturwissenschaften 1933, 21, 787–788. [Google Scholar] [CrossRef]
2. Tinkham, M. Introduction to Superconductivity, 2nd ed.; Dover Publications Inc.: New York, USA, 1996. [Google Scholar]
3. Savitskii, E. M.; Baron, V. V.; Efimov, Yu. V.; Bychkova, M. I.; Myzenkova, L. F. Superconducting Materials, 1st ed.; Plenum Press: New York, London, 1973. [Google Scholar]
4. Rose-Innes, A.C.; Rhoderick, E.H. Introduction to Superconductivity, 2nd ed.; Pergamon Press plc.: Oxford, U.K, 1978. [Google Scholar]
5. Huebener, R. P. Magnetic Flux Structures in Superconductors, 2nd ed.; Springer: Heidelberg, Germany, 2001. [Google Scholar]
6. Poole, C. P. (ed.) Handbook of Superconductivity, 1st ed.; Elsever: Amsterdam, The Netherlands, 1995. [Google Scholar]
7. Buckel, W.; Kleiner, R. Supraleitung. Grundlagen und Anwendungen, 7th ed.; Wiley-VCH: Weinheim, Germany, 2013. [Google Scholar] [CrossRef]
8. Koblischka, M. R. Magnetic properties of high-temperature superconductors; Alpha Science International Ltd.: Oxford, UK, 2009. [Google Scholar]
9. Pitaevskii, L. Phenomenology and Microscopic Theory: Theoretical Foundations. In Superconductivity. Conventional and Unconventional Superconductors, Vol. 1; Bennemann, K.H., Ketterson, J.B., Eds.; Springer: Berlin, Heidelberg, 2008. [Google Scholar]
10. Mangin, P.; Kahn, R. Superconductivity. An Introduction; Springer: Cham, Switzerland, 2017. [Google Scholar]
11. Svedlindh, P.; Niskanen, K.; Norling, P.; Nordblad, P.; Lundgren, L.; Lönnberg, B.; Lundström, T. Anti-Meissner Effect in the BiSrCaCuO System. Physica C 1989, 162–164, 1365–1366. [Google Scholar] [CrossRef]
12. Blunt, F. J.; Perry, A. R.; Campbell, A. M.; Liu, R. S. An investigation of the appearance of positive magnetic moments on field cooling some superconductors. Physica C 1991, 175, 539–544. [Google Scholar] [CrossRef]
13. Braunisch, W.; Knauf, N.; Kataev, V.; Neuhausen, S.; Grütz, A.; Kock, A.; Roden, B.; Khomskii, D.; Wohlleben, D. Paramagnetic Meissner Effect in Bi High-Temperature Superconductors. Phys. Rev. Lett. 1992, 68, 1908–1911. [Google Scholar] [CrossRef]
14. Braunisch, W.; Knauf, N.; Bauer, G.; Kock, A.; Becker, A.; Freitag, B.; Grütz, A.; Kataev, V.; Neuhausen, S.; Roden, B.; Khomskii, D.; Wohlleben, D. Paramagnetic Meissner effect in high-T_c superconductors. Phys. Rev. B 1993, 48, 4030–4042. [Google Scholar] [CrossRef]
15. Kusmartsev, F. V. Destruction of the Meissner effect in granular high-temperature superconductors. Phys. Rev. Lett. 1992, 69, 2268–2271. [Google Scholar] [CrossRef]
16. Heinzel, C.; Theilig, T.; Ziemann, P. Paramagnetic Meissner effect analyzed by second harmonics of the magnetic susceptibility: consistency with a ground state carrying spontaneous currents. Phys. Rev. B 1993, 48, 3445–3454. [Google Scholar] [CrossRef]
17. Riedling, S., Bräuchle, G., Lucht, R., Röhberg, K., v. Löhneysen, H., Claus, H., Erb, A., Müller-Vogt, G. Observation of the Wohlleben effect in YBa₂Cu₃O_7-δ single crystals. Phys. Rev. B 1994 49, 13283-13286. [CrossRef]
18. Khomskii, D. Wohlleben effect (Paramagnetic Meissner effect) in high-temperature superconductors. J. Low Temp. Phys. 1994, 95, 205–223. [Google Scholar] [CrossRef]
19. Niskanen, K.; Magnusson, J.; Svedlindh, P.; Ullström, A.-S.; Lundström, T. Anti-Meissner effect and low magnetic relaxation in sintered Bi-2212. Physica B 1994 194-196, 1549-1550. [CrossRef]
20. Chen, D.-X.; Hernando, A. Paramagnetic Meissner effect and 0-π Josephson junctions. Europhys. Lett. 1994, 26, 365–370. [Google Scholar] [CrossRef]
21. Dominguez, D.; Jagla, E. A.; Balseiro, C. A. Phenomenological theory of the paramagnetic Meissner effect. Phys. Rev. Lett. 1994, 72, 2773–2776. [Google Scholar] [CrossRef]
22. Kötzler, J.; Baumann, M.; Knauf, N. , Complete inversion of the Meissner effect in Bi₂Sr₂CaCu₂O_8+δ ceramics. Phys. Rev. B 1995, 52, 1215–1218. [Google Scholar] [CrossRef]
23. Chen, F.H.; Horng, W.C.; Hsu, H.T.; Tseng, T.Y. Paramagnetic Meissner effect of high-temperature granular superconductors - Interpretation by anisotropic and isotropic models. J. Supercond. 1995, 8, 43–56. [Google Scholar] [CrossRef]
24. Magnusson, J.; Papadopoulou, E.; Svedlindh, P.; Nordblad, P. AC susceptibility of a paramagnetic Meissner effect sample. Physica C 1998, 297, 317–325. [Google Scholar] [CrossRef]
25. Thompson, D. J.; Minhaj, M. S. M.; Wenger, L. E.; Chen, J. T. Observation of Paramagnetic Meissner Effect in Niobium Disks, Phys. Rev. Lett. 1995, 75, 529–532. [Google Scholar] [CrossRef]
26. Minhaj, M. S. M.; Thompson, D. J.; Wenger, L. E.; Chen, J. T. Paramagnetic Meissner Effect in a Niobium Disk. Physica C 1995 235-240, 2519-2520.
27. Kostić, P.; Veal, B.; Paulikas, P.; Welp, U.; Todt, V. K.; Gu, C.; Geiser, U.; Williams, J. M.; Carlson, K. D.; Klemm, R. A. Paramagnetic Meissner effect in Nb. Phys. Rev. B 1996, 53, 791–801. [Google Scholar] [CrossRef]
28. Rice, T. M.; Sigrist, M. Comment on `Paramagnetic Meissner effect in Nb’. Phys. Rev. B 1997, 55, 14647–14648. [Google Scholar] [CrossRef]
29. Kostić, P.; Veal, B.; Paulikas, P.; Welp, U.; Todt, V. K.; Gu, C.; Geiser, U.; Williams, J. M.; Carlson, K. D.; Klemm, R. A. Reply to Comment on `Paramagnetic Meissner effect in Nb’. Phys. Rev. B 1997, 55, 14649–14652. [Google Scholar] [CrossRef]
30. Thompson, D. J.; Wenger, L. E.; Chen, J. T. Inducing and enhancing the paramagnetic Meissner effect in Nb disks. Czech J. Phys. 1996, 46, 1195–1196. [Google Scholar] [CrossRef]
31. Thompson, D. J.; Wenger, L. E.; Chen, J. T. Paramagnetic Meissner effect in conventional Nb superconductors. J. Low Temp. Phys. 1996, 105, 509–514. [Google Scholar] [CrossRef]
32. Thompson, D. J.; Wenger, L. E.; Chen, J. T. Inducing the paramagnetic Meissner effect in Nb disks by surface ion implantation. Phys. Rev. B 1996, 54, 16096–16100. [Google Scholar] [CrossRef]
33. Charnaya, E. V.; Lee, M. K.; Ciou, Y. S.; Tien, C.; Chang, L. J.; Kumzerov, Yu. A. Paramagnetic response in a Pb-porous glass nanocomposite superconductor. Physica C 2013, 495, 221–224. [Google Scholar] [CrossRef]
34. Chu, S.; Schwartz, A. J.; Massalski, T. B.; Laughlin, D. E. Extrinsic paramagnetic Meissner effect in multiphase indium-tin alloys. Appl. Phys. Lett. 2006, 89, 111903. [Google Scholar] [CrossRef]
35. de Lima, O.F.; Avila, M.A.; Cardoso, C.A. Study of paramagnetic frozen states in superconducting Nb and Ta samples. Physica C 1997, 282-287, 2201–2202. [Google Scholar] [CrossRef]
36. Dmitriev, V.M.; Terekhov, A.V.; Zaleski, A.; Khatsko, E.N.; Kalinin, P.S.; Rykova, A.I.; Gurevich, A.M.; Glagolev, S.A.; Khlybov, E.P.; Kostyleva, I.E.; Lachenkov, S.A. The Volleben effect in magnetic superconductors Dy_1–xY_xRh₄B₄ (x= 0.2, 0.3, 0.4, and 0.6). Low Temp. Phys. 2012, 38, 154–156. [Google Scholar] [CrossRef]
37. Ge, J.Y.; Gladilin, V.N.; Sluchanko, N.E.; Lyashenko, A.; Filipov, V.B.; Indekeu, J.O.; Moshchalkov, V.V. Paramagnetic Meissner effect in ZrB₁₂ single crystal with non-monotonic vortex-vortex interactions. New. J. Phys. 2017, 19, 093020; [Google Scholar] [CrossRef]
38. Matin, M.; Sharath Chandra, L. S.; Chattopadhyay, M. K.; Singh, M. N.; Sinha, A. K.; Roy, S. B. High field paramagnetic effect in the superconducting state of Ti_0.8V_0.2 alloy. Supercond. Sci. Technol. 2013, 26, 115005. [Google Scholar] [CrossRef]
39. Nakagawa, M.; Utsumi, S.; Hirayama, T.; Sumiyama, A.; Oda, Y. Measurement of paramagnetic Meissner effect in s-wave superconductor. J. Magn. Magn. Mat. 1998 177-181, 533-534. [CrossRef]
40. Nakagawa, M.; Utsumi, S.; Oda, Y. Maximum magnetic moment in a field-cooled superconducting disk. Phys. Rev. B 1999, 60, 1372–1376. [Google Scholar] [CrossRef]
41. Kumar, S.; Tomy, C. V.; Balakrishnan, G.; McK Paul, D.; Grover, A. K. Paramagnetic magnetization signals and curious metastable behaviour in field-cooled magnetization of a single crystal of superconductor 2H-NbSe. J. Phys. Condensed Matteer 2015, 27, 295701. [Google Scholar] [CrossRef]
42. Proslier, T.; Kharitonov, M.; Pellin, M.; Zasadzinski, J.; Ciovati, G. Evidence of Surface Paramagnetism in Niobium and Consequences for the Superconducting Cavity Surface Impedance. IEEE Trans. Appl. Supercond. 2011, 21, 2619–2622; [Google Scholar] [CrossRef]
43. Sharma, M. M.; Kumar, K.; Sang, L.N.; Wang, X. L.; Awana, V. P. S. Type-II superconductivity below 4 K in Sn0.4Sb0.6. J. Alloys Compounds 2020, 844, 156140; [Google Scholar] [CrossRef]
44. Smolyak, B.M.; Ermakov, G.V. The paramagnetic effect of clusters in granular superconductors under the Meissner magnetization. J. Magn. Magn. Mat. 1996, 153, 311–314. [Google Scholar] [CrossRef]
45. Sundar, S.; Chattopadhyay, X.; Sharath Chandra, L. S.; Roy, S. B. High field paramagnetic Meissner effect in Mo_100-xRe_x alloy superconductors. Supercond. Sci. Technol. 2015, 28, 075011. [Google Scholar] [CrossRef]
46. Suresh Babu, M.; Thamizhavel, A.; Ramakrishnan, S.; Grover, A.K.; Pal, D. Switching effect in the magnetization response in a superconducting specimen of Ca₃Rh₄Sn₁₃. J. Phys. D: Appl. Phys. 2016, 49, 185502. [Google Scholar] [CrossRef]
47. Takeya, H. , Massalami, M. E., Amorim, H. S., Fujii, H., Mochiku, T., and Takano, Y. On the superconductivity of the Li_xRhB_y compositions. Mater. Res. Expr. 2014, 1, 046001. [Google Scholar] [CrossRef]
48. Zhang, L.Z.; Zhang, A.L.; Lu, W.L.; Xiao, Q.L.; Chen, F.; Feng, Z.; Cao, S.X.; Zhang, J.C.; Ge, J.-Y. Paramagnetic Meissner Effect Observed in SrBi₃ with kappa Close to the Critical Regime. J. Supercond. Novel. Magn. 2020, 33, 1691–1695. [Google Scholar] [CrossRef]
49. Aliev, A. E.; de Andrade, M. J.; Salamon, M. B. Paramagnetic Meissner effect in electrochemically doped indium-tin oxide films. J. Supercond. Nov. Magn. 2016, 29, 1793–1803. [Google Scholar] [CrossRef]
50. Brandt, D.; Binns, C.; Gurman, S. J.; Torricelli, G.; Gray, D. S. W. Paramagnetic Meissner transitions in Pb films and the vortex compression model. J. Low Temp. Phys. 2011, 163, 170–175. [Google Scholar] [CrossRef]
51. Sandim, M. J. R., Stamopoulos, D., Ghivelder, L., Lim, S. C. V., and Rollett, A. D. Paramagnetic Meissner effect and AC magnetization in roll-bonded Cu-Nb layered composites. J. Supercond. Nov. Magn. 2010 23, 1533-1541. [CrossRef]
52. Terentiev, A., Watkins, D. B., De Long, L. E., Morgan, D. J., and Ketterson, J. B. Paramagnetic relaxation and Wohlleben effect in field-cooled Nb thin films. Phys. Rev. B 1999 60, R761-R764. [CrossRef]
53. Yuan, S., Ren, L., and Li, F. Paramagnetic Meissner effect in Pb nanowire arrays. Phys. Rev. B 2004 69, 092509. [CrossRef]
54. Bawa, A.; Gupta, A.; Singh, S.; Awana, V. P. S.; Sahoo, S. Ultrasensitive interplay between ferromagnetism and superconductivity in NdGd composite thin films. Sci. Rep. 2016, 6, 18689. [Google Scholar] [CrossRef]
55. Chuang, T.M.; Lee, S.F.; Huang, S.Y.; Yao, Y.D.; Cheng, W.C.; Huang, G.R. Anomalous magnetic moments in Co/Nb multilayers. J. Magn. Magn. Mat. 2002, 239, 301–303. [Google Scholar] [CrossRef]
56. Di Bernardo, A.; Salman, Z.; Wang, X.L.; Amado, M.; Egilmez, M.; Flokstra, M.G.; Suter, A.; Lee, S.L.; Zhao, J.H.; Prokscha, T.; Morenzoni, E.; Blamire, M.G.; Linder, J.; Robinson, J.W.A. Intrinsic Paramagnetic Meissner Effect Due to s-Wave Odd-Frequency Superconductivity. Phys. Rev. X 2015, 5, 041021. [Google Scholar] [CrossRef]
57. Nagy, B.; Khaydukov, Y.; Efremov, D.; Vasenko, A. S.; Mustafa, L.; Kim, J. -H.; Keller, T.; Zhernenkov, K.; Devishvili, A.; Steitz, R.; Keimer, B.; Bottyan, L. On the explanation of the paramagnetic Meissner effect in superconductor/ferromagnet heterostructure. Europhys. Lett. 2016, 116, 17005. [CrossRef]
58. Nielsen, A. P.; Cawthorne, A. B.; Barbara, P.; Wellstood, F. C.; Lobb, C. J.; Newrock, R. S.; Forrester, M. G. Paramagnetic Meissner effect in multiply-connected superconductors. Phys. Rev. B 2000, 62, 14380–14383. [Google Scholar] [CrossRef]
59. Nielsen, A.P.; Holzer, J.; Cawthorne, A.B.; Lobb, C.J.; Newrock, R.S.; Markus, J. The paramagnetic Meissner effect in Nb/AlOx/Nb Josephson junction arrays. Physica B 2000, 280, 444–445; [Google Scholar] [CrossRef]
60. Zhou, H.; Gong, X.; Jin, X. Magnetic properties of superconducting Bi/Ni bilayers. J. Magn. Magn. Mat. 2017, 422, 73–76. [Google Scholar] [CrossRef]
61. He, Q.; He, M.; Shen, J.; Lai, Y.; Liu, Y.; Liu, H.; He, H.; Wang, G.; Wang, J.; Lortz, R.; Sou, I. Anisotropic magnetic responses of a 2D-superconducting Bi₂Te₃/FeTe heterostructure. J. Phys.: Condens. Matter 2015, 27, 345701. [Google Scholar] [CrossRef]
62. Xing, Y. T., Miklitz, H., and Baggio-Saitovich, E. Controlled switching between paramagnetic and diamagnetic Meissner effects in superconductor-ferromagnet Pb-Co nanocomposites. Phys. Rev. B 2009 80, 224505. [CrossRef]
63. Geim, A. K.; Dubonos, S. V.; Lok, J. G. S.; Henini, M.; Maan, J. C. Paramagnetic Meissner effect in small superconductors. Nature 1998, 396, 144–146. [Google Scholar] [CrossRef]
64. Müller-Allinger, F.B.; Mota, A.C. Paramagnetic Reentrant Effect in High Purity Mesoscopic AgNb Proximity Structures. Phys. Rev. Lett. 2000, 84, 3161–3164. [Google Scholar] [CrossRef]
65. Kanda, A.; Ootuka, Y. Response of a mesoscopic superconducting disk to magnetic fields. Microelectronic Eng. 2002, 63, 313–317. [Google Scholar] [CrossRef]
66. Kanda, A.; Ootuka, Y. Paramagnetic supercurrent and transition points between different vortex states in mesoscopic superconducting disks. Physica C 2004, 404, 205–208. [Google Scholar] [CrossRef]
67. A. Kanda,1,* B. J. Baelus,2,3,† F. M. Peeters,3 K. Kadowaki,2 and Y. Ootuka1 Experimental Evidence for Giant Vortex States in a Mesoscopic Superconducting Disk. Phys. Rev. Lett. 2004 93, 257002. [CrossRef]
68. Nagamatsu, J.; Nakagawa, N.; Muranaka, T.; Zenitani, Y.; Akimitsu, J. Superconductivity at 39 K in magnesium diboride. Nature 2001, 410, 63–64. [Google Scholar] [CrossRef]
69. Buzea, C.; Yamashita, T. Review of the superconducting properties of MgB₂. Supercond. Sci. Technol. 2001, 14, R115–R146. [Google Scholar] [CrossRef]
70. Passos, W. A. C.; Lisboa-Filho, P. N.; Fraga, G. L.; Fabris, F. W.; Purreur, P.; Ortiz, W. A. Paramagnetic Meissner effect and magnetic remanence in granular MgB₂. Brazil. J. Phys. 2002, 32, 777–779. [Google Scholar] [CrossRef]
71. Sözeri, H.; Dorosinskii, L.; Topal, U.; Ercan, I. Paramagnetic Meisser effect in MgB₂. Physica C 2004 408-410, 109-11. [CrossRef]
72. Prokhorov, V. G.; Kaminsky, G. G.; Svetchnikov, V. L.; Park, J. S.; Eom, T. W.; Lee, Y. P.; Kang, J.-H.; Khokhlov, V. A.; Mikheenko, P. Flux pinning and vortex dynamics in MgB₂ doped with TiO₂ and SiC inclusions. Low Temp. Phys. 2009, 35, 439–448. [Google Scholar] [CrossRef]
73. Prokhorov, V. G.; Svetchnikov, V. L.; Park, J. S.; Kim, G. H.; Lee, Y. P.; Kang, J.-H.; Khokhlov, V. A.; Mikheenko, P. Flux pinning and the paramagnetic Meissner effect in MgB₂ with TiO₂ inclusions. Supercond. Sci. Technol. 2009, 22, 045027. [Google Scholar] [CrossRef]
74. Kuroda, T.; Nakane, T.; Kumakura, H. Effects of doping with nanoscale Co₃O₄ particles on the superconducting properties of powder-in-tube processed MgB₂ tapes. Physica C 2009, 469, 9–14. [Google Scholar] [CrossRef]
75. Singh, D. S., Tiwari, B., Jha, R., Kishan, H., and Awana, V. P. S. Role of MgO impurity on the superconducting properties of MgB₂. Physica C 2014, 505, 104–108. [CrossRef]
76. Govindaraj, L.; Arumugam, S.; Thiyagarajan, R.; Kumar, D.; Kannan, M.; Das, D.; Suraj, T.S.; Sankaranarayanan, V.; Sethupathi, K.; Baskaran, G.; Sankar, R.; Rao, M.M.C.D. Wohlleben Effect and Emergent 7C junctions in superconducting Boron doped Diamond thin films. Physica C 2022, 598, 1354065; [Google Scholar] [CrossRef]
77. Asano, Y.; Sasaki, A. Odd-frequency Cooper pairs in two-band superconductors and their magnetic response. Phys. Rev. B 2015, 92, 224508. [Google Scholar] [CrossRef]
78. Barbara, P.; Araujo-Moreira, F.M.; Cawthorne, A. B.; Lobb, C. J. Reentrant ac magnetic susceptibility in Josephson-junction arrays: An alternative explanation for the paramagnetic Meissner effect. Phys. Rev. B 1999, 60, 7489–7495. [Google Scholar] [CrossRef]
79. Chaban, I. A. Paramagnetic Meissner effect. J. Supercond. Nov. Magn. 2000, 13, 1011–1017. [Google Scholar] [CrossRef]
80. He, Y.; Muirhead, C. M.; Vinen, W. F. Paramagnetic Meissner effect in high-temperature superconductors: experiments and interpretation. Phys. Rev. B 1996, 53, 12441–12453. [Google Scholar] [CrossRef]
81. He, Y.; Muirhead, C. M.; Vinen, W. F. Paramagnetic Meissner effect of high T_c superconductors (I). Science in China 1998, 41, 647–655. [Google Scholar] [CrossRef]
82. He, Y.; Muirhead, C. M.; Vinen, W. F. Paramagnetic Meissner effect of high T_c superconductors (II). Science in China 1998, 41, 762–772. [Google Scholar] [CrossRef]
83. Higashitani, S. Mechanism of paramagnetic Meissner effect in high-temperature superconductors. J. Phys. Soc. Jpn. 1997, 66, 2556–2559. [Google Scholar] [CrossRef]
84. Kallio, A.; Sverdlov, V.; Rytivaara, M. Paramagnetic Meissner effect and time-reversal non-invariance from spin polarization. Superlatt. Microstruct. 1997, 21, 481–486. [Google Scholar] [CrossRef]
85. Koshelev, A. E.; Larkin, A. I. Paramagnetic moment in field-cooled superconducting plates: Paramagnetic Meissner effect. Phys. Rev. B 1995, 52, 13559–13562. [Google Scholar] [CrossRef]
86. Lebed, A. G. , Paramagnetic intrinsic Meissner effect in a bulk. JETP Lett. 2008, 88, 201–204. [Google Scholar] [CrossRef]
87. Lebed, A. G. , Paramagnetic intrinsic Meissner effect in layered superconductors. Phys. Rev. B 2008, 78, 012506. [Google Scholar] [CrossRef]
88. Moshchalkov, V. V.; Qiu, X. G.; Bruyndoncx, V. Paramagnetic Meissner effect from the self-consistent solution of the Ginzburg-Landau equations. Phys. Rev. B 1997 55, 11793-11801.
89. Moshchalkov, V. V.; Qiu, X. G.; Bruyndoncx, V. The paramagnetic Meissner effect resulting from the persistence of the giant vortex state. J. Low Temp. Phys. 1996, 105, 515–520. [Google Scholar] [CrossRef]
90. Obukhov, Yu. V. The ”Paramagnetic” Meissner effect in superconductors. J. Supercond. 1998, 11, 733–736. [Google Scholar] [CrossRef]
91. Ortiz, W. A.; Lisboa-Filho, P. N.; Passos, W. A. C.; Araujo-Moreira, F. M. Field-induced networks of weak-links: an experimental demonstration that the paramagnetic Meissner effect is inherent to granularity. Physica C 2001, 361, 267–273. [Google Scholar] [CrossRef]
92. Schweigert, V. A.; Peeters, F. M. Field-cooled vortex states in mesoscopic superconducting samples. Physica C 2000, 332, 426–431. [Google Scholar] [CrossRef]
93. Schweigert, V. A.; Peeters, F. M. Phase transitions in thin mesoscopic superconducting disks. Phys. Rev. B 1998, 57, 13817–13832. [Google Scholar] [CrossRef]
94. Sergeenkov, S. Polarization effects induced by a magnetic field in intrinsically granular superconductors. J. Exp. Theo. Phys. 2005, 101, 919–925. [Google Scholar] [CrossRef]
95. Sigrist, M., Rice, T. M. Unusual paramagnetic phenomena in granular high-temperature superconductors – A consequence of d-wave pairing? Rev. Mod. Phys. 1995, 67, 503–513. [CrossRef]
96. Tempere, J., Gladilin, V. N., Silvera, I. F., Devreese, J. T., Moshchalkov, V. V. Coexistence of the Meissner and vortex states on a nanoscale superconducting spherical shell. Phys. Rev. B 2009, 79, 134516. [CrossRef]
97. Zha, G.-Q., Zhou, S.-P., Zhu, B.-H., Shi, Y.-M. Charge distribution in thin mesoscopic superconducting rings with enhanced surface superconductivity. Phys. Rev. B 2006, 73, 104508. [CrossRef]
98. Zharkov, G. F. Paramagnetic Meissner effect in superconductors from self-consistent solution of Ginzburg-Landau equations. Phys. Rev. B 2001, 63, 214502. [Google Scholar] [CrossRef]
99. Zhu, B.-H., Zhou, S.-P., Shi, Y.-M., Zha, G.-Q., Yang, K. Influence of de Gennes boundary conditions on the charge distribution of the Meissner state and the single-vortex state in thin mesoscopic rings. Phys. Rev. B 2006 74, 014501. [CrossRef]
100. Li, M.S. Paramagnetic Meissner effect and related dynamical phenomena. Phys. Rep. 2003, 376, 133–223. [Google Scholar] [CrossRef]
101. Koblischka, M.R.; Pust, L.; Chikumoto, N.; Murakami, M.; Nilsson, B.; Claeson, T. Paramagnetic Meissner response of an artificially granular YBCO thin film. Physica B 2000, 284-288, 599–600. [Google Scholar] [CrossRef]
102. Koblischka, M.R.; Pust, L.; Galkin, A.; Nalevka, P.; Jirsa, M.; Johansen, T.H.; Bratsberg, H.; Nilsson, B.; Claeson, T. Flux penetration into an artificially granular high-T_c superconductor. Phys. Rev. B 1999, 59, 12114–12120. [Google Scholar] [CrossRef]
103. Koblischka, M. R.; Pust, L.; Chikumoto, N.; Murakami, M.; Nilsson, B.; Claeson, T. Paramagnetic Meissner response of an artificially granular YBCO thin film. Physica B 2000, 284-288, 599–600. [Google Scholar] [CrossRef]
104. Kirtley, J. R.; Mota, A. C.; Sigrist, L.; Rice, T. M. Magnetic imaging of the paramagnetic Meissner effect in the granular high-T_c superconductor Bi₂Sr₂CaCu₂O_x. J. Phys.: Condens. Matter. 1998 10, L97-L103. [CrossRef]
105. Gross, R. private communication with Kirtley, J.R.
106. Magnusson, J.; Nordblad, P.; Svedlindh, P. Zero-field flux noise in granular Bi₂Sr₂CaCu₂O₈. Physica C 1997, 282-287, 2369-2370. [CrossRef]
107. Pessoa, A.L.; Koblischka-Veneva, A.; Carvalho, C.L.; Zadorosny, R.; Koblischka, M.R. Paramagnetic Meissner Effect and Current Flow in YBCO Nanofiber Mats. IEEE Trans. Appl. Supercond. 2021, 31, 7200105. [Google Scholar] [CrossRef]
108. Pessoa, A.L.; Koblischka-Veneva, A.; Carvalho, C. L.; Zadorosny, R.; Koblischka, M. R. Microstructure and paramagnetic Meissner effect of YBa₂Cu₃0_y nanowire networks. J. Nanoparticle Res. 2020, 22, 360. [Google Scholar] [CrossRef]
109. Dias, F.T.; Pureur, P.; Rodrigues, P.; Obradors, X. High-field paramagnetic Meissner effect in melt-textured YBCO. Physica C 2004, 408, 653–654. [Google Scholar] [CrossRef]
110. Gouvea, C.; Dias, F.T.; Vieira, V.D.; da Silva, D.L.; Schaf, J.; Wolff-Fabris, F.; Rovira, J.J.R. Paramagnetic Meissner effect and strong time dependence at high fields in melt-textured high-T(C) superconductors. J. Korean Phys. Soc. 2013, 62, 1414–1417. [Google Scholar] [CrossRef]
111. Rykov, A.I.; Tajima, S.; Kusmartsev, F.V. High-field paramagnetic effect in large crystals of YBa₂Cu₃0_7-δ. Phys. Rev. B 1997, 55, 8557–8563. [Google Scholar] [CrossRef]
112. Koblischka, M.R.; Muralidhar, M.; Higuchi, T.; Waki, K.; Chikumoto, N.; Murakami, M. Superconducting transitions of Nd-based 123 superconductors in fields up to 7 T. Supercond. Sci. Technol. 1999, 12, 288–292. [Google Scholar] [CrossRef]
113. Koblischka, M.R.; Murakami, M. Magnetic Properties of Superconducting and Nonsuperconducting (Nd_0.33Eu_0.33Gd_0.33)Ba₂Cu₃O_y. J. Supercond. Novel Magn. 2001, 14, 415–419. [Google Scholar] [CrossRef]
114. Pust, L.; Wenger, L. E.; Koblischka, M. R. Detailed investigation of the superconducting transition of niobium disks exhibiting the paramagnetic Meissner effect. Phys. Rev. B 1998, 58, 14191–14194. [Google Scholar] [CrossRef]
115. Pust, L.; Wenger, L. E.; Koblischka, M. R. Details of the Superconducting Phase Transition in Nb showing the Paramagnetic Meissner Effect. Phys. stat. solidi (b) 1999, 212, R13–R14. [Google Scholar] [CrossRef]
116. Fodor, P. S.; Wenger, L. E. Paramagnetic Meissner effect in Nb disks. Physica C 2000, 341-348, 2043–2044. [Google Scholar] [CrossRef]
117. Wenger, L. E.; Pust, L.; Koblischka, M. R. Investigation of the paramgnetic Meissner effect on Nb disks. Physica B 2000, 284-288, 797–798. [Google Scholar] [CrossRef]
118. Papadopoulou, E.L.; Nordblad, P.; Svedlindh, P.; Schoneberger, R.; Gross, R. The ageing effect in a superconducting sample displaying the paramagnetic Meissner effect. Physica C 1999, 317, 637–639. [Google Scholar] [CrossRef]
119. Papadopoulou, E.L.; Svedlindh, P.; Nordblad, P. Flux dynamics of a superconductor showing a glassy paramagnetic Meissner state. Phys.Rev. B 2002, 65, 144524. [Google Scholar] [CrossRef]
120. Bhat, S. V.; Rastogi, A.; Kumar, N.; Nagarajan, R.; Rao, C. N. R. Paramagnetic Meissner effect in YBa₂Cu₃0_7-δ. Physica C 1994, 219, 87–92. [Google Scholar] [CrossRef]
121. Luzhbin, D. A.; Pan, A. V.; Komashenko, V. A.; Flis, V. S.; Pan, V. M.; Dou, S. X.; Esquinazi, P. Origin of paramagnetic magnetization in field-cooled YBa₂Cu₃O_7-δ films. Phys. Rev. B 2004, 69, 024506. [Google Scholar] [CrossRef]
122. Prusseit, W.; Walter, H.; Semerad, R.; Kinder, H.; Assmann, W.; Huber, H.; Kabius, B.; Burkhardt, H.; Rainer, D.; Sauls, J. A. Observation of paramagnetic Meissner currents – evidence for Andreev bound surface states. Physica C 1999 317-318, 396-402. [CrossRef]
123. Tsoy, G. M.; Janu, Z.; Novak, M. Paramagnetic Meissner effect in YBa₂Cu₃O₇: influence of AC magnetic field and magnetic relaxation. Physica B 2000 284-288, 811-812. [CrossRef]
124. Felner, I.; Tsindlekht, M.I.; Drachuck, G.; Keren, A. Anisotropy of the upper critical fields and the paramagnetic Meissner effect in La_1.85Sr_0.15CuO₄ single crystals. J. Phys.: Condens. Matter 2013, 25, 065702. [Google Scholar] [CrossRef]
125. Okram, G.S.; Adroja, D.T.; Padalia, B.D. The paramagnetic Meissner effect in Nd_2-xCe_xCuO_y superconductors at 40 G and flux trapping. J. Phys. Cond. Matt. 1997, 9, L525–L531. [Google Scholar] [CrossRef]
126. Kim, H.T.; Minami, H.; Schmidbauer, W.; Hodby, J.W.; Iyo, A.; Iga, F.; Uwe, H. Paramagnetic Meissner effect in superconducting single crystals of Ba_1-xK_xBiO₃. J. Low. Temp. Phys. 1996, 105, 557–562. [Google Scholar] [CrossRef]
127. Awana, V. P. S.; Menon, L.; Malik, S. K. Synthesis, superconductivity and magnetism of RSr₂Cu₂Nb0_7-δ compounds (R= Y, Pr, and Gd). Physica C 1996, 262, 266–271. [Google Scholar] [CrossRef]
128. Liu, Y.; Zhou, L.; Sun, K.W.; Straszheim, W.E.; Tanatar, M.A.; Prozorov, R.; Lograsso, T.A. Doping evolution of the second magnetization peak and magnetic relaxation in (Ba_1-xK_x)Fe₂As₂ single crystals. Phys. Rev. B 2018, 97, 054511; [Google Scholar] [CrossRef]
129. Eisterer, M. Magnetic properties and critical currents of MgB₂. Supercond. Sci. Technol. 2007, 20, R47–R74. [Google Scholar] [CrossRef]
130. Koblischka, M.R.; Wiederhold, A.; Koblischka-Veneva, A.; Chang, C.; Berger, K.; Nouailhetas, Q.; Douine, B.; Murakami, M. On the origin of the sharp, low-field pinning force peaks in MgB₂ superconductors. AIP Adv. 2020, 10, 015035. [Google Scholar] [CrossRef]
131. Narlikar, A. V. Superconductors, Oxford University Press: Oxford, U.K., 2014.
132. Atzmony, U., Bennett, L. H., Swartzendruber, L. J. Is there is a paramagnetic Meissner effect? IEEE Trans. Magn. 1995, 31, 4118–4120. [CrossRef]
133. McElfresh, SQUID magnetometry, brochure, Quantum Design, CA.
134. Quantum Design, San Diego, CA. SQUID models MPMS-5, MPMS-XL, MPMS3 with various options (ultra-low field option, VSM option, AC susceptibility).
135. Thompson, D. J. PhD work, University of Michigan, Detroit, USA, 1996.
136. Weber, H.W.; Schachinger, E. H_c2-anisotropy effects in superconducting niobium polycrystals. Helvetica Physica Acta 1988, 61, 478–487. [Google Scholar]
137. Koblischka, M.R.; Koblischka-Veneva, A. Magnetic properties of superconductors. In: Superconducting Materials. Fundamentals, Synthesis and Applications; Slimani, Y.; Hannachi, E.; Springer-Nature, Singapore, 2022, Chap. 3, pp. 61-88.
138. Koblischka, M.R.; Pust, L.; Jirsa, M.; Johansen, T.H. Formation of the low-field peak in magnetization loops of high-T_c superconductors. Physica C 1999, 320, 101–114. [Google Scholar] [CrossRef]
139. Shantsev, D.V.; Koblischka, M.R.; Galperin, Y.M.; Johansen, T.H.; Pust, L.; Jirsa, M. Central Peak Position in Magnetization Loops of High-T_c Superconductors. Phys. Rev. Lett. 1999, 82, 2947–2950. [Google Scholar] [CrossRef]
140. Halbritter, J. Low temperature oxidation of Nb and of Nb-compounds in relation to superconducting application. J. Less-Common Met. 1988, 139, 133–148. [Google Scholar] [CrossRef]
141. Koblischka, M. R.; Chang, C.S.; Pust, L. The PME in Nb: 20 years after. submitted to Europhys. Lett.
142. Koblischka, M. R.; Wijngaarden, R. J. Magneto-optical investigations of superconductors. Supercond. Sci. Technol. 1995, 8, 199–213. [Google Scholar] [CrossRef]
143. Jooss, C.; Albrecht, J.; Kuhn, H.; Leonhardt, S.; Kronmüller, H. Magneto-optical studies of current distributions in high-T_c superconductors. Rep. Prog. Phys. 2002, 65, 651–788. [Google Scholar] [CrossRef]
144. Kirtley, J. R.; Tsuei, C. C.; Rupp, M.; Sun, J. Z.; Yu-Jahnes, L.S.; Gupta, A.; Ketchen, M. B.; Moler, K. A.; Bhushan, M. Direct Imaging of Integer and Half-Integer Josephson Vortices in High-T_c Grain Boundaries. Phys. Rev. Lett. 1996, 76, 1336–1339. [Google Scholar] [CrossRef] [PubMed]
145. Kirtley, J.R. Fundamental studies of superconductors using scanning magnetic imaging. Rep. Prog. Phys. 2010, 73, 126501. [Google Scholar] [CrossRef]
146. Rondin, L.; Tetienne, J.-P.; Hingant, T.; Roch, J.-F.; Maletinsky, P.; Jacques, V. Magnetometry with nitrogen-vacancy defects in diamond. Rep. Prog. Phys. 2014, 77, 056503. [Google Scholar] [CrossRef] [PubMed]
147. Doherty, M.W.; Manson, N.B.; Delaney, P.; Jelezko, F.; Wrachtrup, J.; Hollenberg, L.C. The nitrogen-vacancy colour centre in diamond. Phys. Rep. 2013, 528, 1–45. [Google Scholar] [CrossRef]
148. Shaw, G.; Blanco Alvarez, S.; Brisbois, J.; Burger, L.; Pinheiro, L. B. L. G.; Kramer, R. B. G.; Motta, M.; Fleury-Frenette, K.; Ortiz, W. A.; Vanderheyden, B.; Silhanek, A. V. Magnetic Recording of Superconducting States. Metals 2019, 9, 1022. [Google Scholar] [CrossRef]
149. Brisbois, J.; Gladilin, V. N.; Tempere, J.; Devreese, J.T.; Moshchalkov, V.V.; Colauto, F.; Motta, M.; Johansen, T.H.; Fritzsche, J.; Adami, O.-A.; Nguyen, N. D.; Ortiz, W. A.; Kramer, R. B. G.; Silhanek, A.V. Flux penetration in a superconducting film partially capped with a conducting layer. Phys. Rev. B 2017, 95, 094506. [Google Scholar] [CrossRef]
150. Nusran, N. M.; Joshi, K.R.; Cho, K.; Tanatar, M.A.; Meier, W. R.; Bud’ko, S. I.; Canfield, P. C.; Liu, Y.; Lograsso, T. A.; Prozorov, R. Spatially-resolved study of the Meissner effect in superconductors using NV-centers-in-diamond optical magnetometry. New J. Phys. 2018, 20, 043010. [Google Scholar] [CrossRef]
151. Suter, A.; Morenzoni, E.; Garifianov, N.; Khasanov, R.; Kirk, E.; Luetkens, H.; Prokscha, T.; Horisberger, M. Observation of Nonexponential Magnetic Penetration Profiles in the Meissner State: A Manifestation of Nonlocal Effects in Superconductors. Phys. Rev. B 2005, 72, 024506. [Google Scholar] [CrossRef]
152. Morenzoni, E.; Wojek, B.M.; Suter, A.; Prokscha, T.; Logvenov, G.; Božović, I. The Meissner Effect in a Strongly Underdoped Cuprate Above Its Critical Temperature, Nat. Commun. 2011, 2, 272. [Google Scholar] [CrossRef]
153. Geim, A.K.; Dubonos, S.V.; Lok, J.G.S.; Grigorieva, I.V.; Maan, J.C.; Theil Hansen, L.; Lindelof, P.E. Ballistic Hall micromagnetometry. Appl. Phys. Lett. 1997, 71, 2379–2381. [Google Scholar] [CrossRef]
154. Schweigert, V.A.; Peeters, F.M. Phase transitions in thin superconducting disks. Phys. Rev. B 1998, 57, 13817–13832. [Google Scholar] [CrossRef]
155. Schweigert, V. A.; Peeters, F. M.; Deo, P. S. Vortex phase diagram for mesoscopic superconducting disks. Phys. Rev. Lett. 1998, 81, 2783–2786. [Google Scholar] [CrossRef]
156. Mishra, P. K.; Ravikumar, G.; Sahni, V. C.; Koblischka, M. R. Grover, A. K. Surface pinning in niobium and a high-T_c superconductor. Physica C 1996, 269, 71–75. [Google Scholar] [CrossRef]
157. Benoist, R.; Zwerger, W. Critical fields of mesoscopic superconductors. Z. Phys. B 1997, 103, 377–381. [Google Scholar] [CrossRef]
158. E. Babaev, E.; Carlström, J.; Silaev, M.; Speight, J.M. Type-1.5 superconductivity in multicomponent system. Physica C 2017, 533, 20–35. [CrossRef]
159. Babaev, E.; Speight, M. Semi-Meissner state and neither type-I nor type-II superconductivity in multicomponent superconductors. Phys. Rev. B 2005, 72, 180502. [Google Scholar] [CrossRef]
160. Moshchalkov, V.; Menghini, M.; Nisho, T.; Chen, Q.H.; Dao, V.H.; Chibotaru, L.F.; Zhigadlo, N.D.; Karpinski, J. Type-1.5 Superconductivity. Phys. Rev. Lett. 2009, 102, 117001. [Google Scholar] [CrossRef]
161. da Silva, R.M.; Milosevic, M.V.; Shanenko, A.A.; Peeters, F.M.; Aguiar, J.A. Giant paramagnetic Meissner effect in multiband superconductors. Sci. Rep. 2015, 5, 12695. [Google Scholar] [CrossRef] [PubMed]
162. da Silva, R. M.; Milošević, M. V.; Shanenko, A. A.; Peeters, F. M.; Albino Aguiar, J. Giant paramagnetic Meissner effect in multiband superconductors. Sci. Rep. 2015, 5, 12695. [Google Scholar] [CrossRef]
163. Zhuravel, A. P.; Bae, S.; Shevchenko, S. N.; Omelyanchouk, A. N.; Lukashenko, A. V.; Ustinov, A. V.; Anlage, S. M. Imaging the paramagnetic nonlinear Meissner effect in nodal gap superconductors. Phys. Rev. B 2018, 97, 054504. [Google Scholar] [CrossRef]
164. Zhang, T.; Cheng, P.; Li, W.-J.; Sun, Y.-J.; Wang, G.; Zhu, X.-G.; Ke, H.; Wang, L.; Ma, X.; Chen, X.; Wang, Y.; Liu, Y.; Lin, H.-Q.; Jia, J.-F.; Xue, Q.-K. Superconductivity in one-atomic-layer metal films grown on Si(111). Nature Phys. 2010, 6, 104–108. [Google Scholar] [CrossRef]
165. Lin, Y.-H.; Nelson, J.; Goldman, A.M. Superconductivity of Very Thin Films: The Superconductor-Insulator Transition. Physica C 2015, 514, 130–141. [Google Scholar] [CrossRef]
166. Nam, H.; Chen, H.; Liu, T.; Kim, J.; Zhang, C.; Yong, J.; Lemberger, T.R.; Kratz, P.A.; Kirtley, J.R.; Moler, K.A.; Adams, P.W.; MacDonald, A.H.; Shih, C.-K. Ultrathin two-dimensional superconductivity with strong spin–orbit coupling. PNAS 2016, 113, 10513–10517. [Google Scholar] [CrossRef]
167. Lei, C.; Chen, H.; MacDonald, A.H. Ultrathin Films of Superconducting Metals as a Platform for Topological Superconductivity. Phys. Rev. Lett. 2018, 121, 227701. [Google Scholar] [CrossRef]
168. Sibanda, D.; Oyinbo, S.T.; Jen, T.-C.; Ibitoye, A.I. A Mini Review on Thin Film Superconductors. Processes 2022, 10, 1184. [Google Scholar] [CrossRef]
169. Koblischka, M.R.; Koblischka-Veneva, A. Superconductivity 2022. Metals 2022, 12, 568. [Google Scholar] [CrossRef]